PC/PET XYLEX™ X5230 BK1G338 SABIC INNOVATIVE US
136
Unit Price:$3737 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High heat resistance Filler: Mineral filler
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 265°C/5.0kg | ASTMD1238 | 28 | g/10min |
| Melt Volume-Flow Rate (MVR) | 265°C/5.0kg | ISO1133 | 24.0 | cm3/10min |
| Shrinkage rate | MD2 | 内部方法 | 0.50to0.60 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.42 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.14 | % | |
| Shrinkage rate | MD2 | 内部方法 | 0.50到0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 14 | kJ/m² |
| Tensile modulus | ISO527-2/1 | 3990 | Mpa | |
| Unscented Izod Impact Strength | 23°C | ISO180/1U | 140 | kJ/m² |
| tensile strength | Yield | ISO527-2/5 | 53.0 | Mpa |
| Break | ISO527-2/5 | 34.0 | Mpa | |
| elongation | Yield | ISO527-2/5 | 3.4 | % |
| Break | ISO527-2/5 | 21 | % | |
| Bending modulus | ISO178 | 3820 | Mpa | |
| Bending stress 3, | ISO178 | 90.0 | Mpa | |
| CharpyNotchedImpactStrength | 23°C | ISO179/1eA | 14 | kJ/m² |
| Suspended wall beam notch impact strength | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 8.0 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | 120 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 100 | °C |
| vicat softening point | -- | ISO306/B50 | 137 | °C |
| -- | ISO306/B120 | 140 | °C | |
| Linear coefficient of thermal expansion | MD：-30to80°C | ISO11359-2 | 4.5E-05 | cm/cm/°C |
| TD：-30to80°C | ISO11359-2 | 9.7E-05 | cm/cm/°C | |
| TD:-30to80°C | ISO11359-2 | 9.7E-05 | cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.