PC/PET X5230 BK1G338 SABIC INNOVATIVE US
XYLEX™
Automotive Applications
Flame retardant、High heat resistance、Filler: Mineral filler
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X5230 BK1G338
Melt Volume-Flow Rate (MVR)
265°C/5.0kg
ISO1133
cm3/10min
2
Melt mass flow rate
265°C/5.0kg
ASTMD1238
g/10min
2
Shrinkage rate
MD2
内部方法
%
0
Shrinkage rate
MD2
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X5230 BK1G338
CharpyNotchedImpactStrength
23°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam gap
23°C
ISO179/1eA
kJ/m²
1
Tensile modulus
ISO527-2/1
Mpa
3
tensile strength
屈服
ISO527-2/5
Mpa
5
tensile strength
断裂
ISO527-2/5
Mpa
3
elongation
屈服
ISO527-2/5
%
3
elongation
断裂
ISO527-2/5
%
2
Bending modulus
ISO178
Mpa
3
Bending stress 3,
ISO178
Mpa
9
Unscented Izod Impact Strength
-30°C
ISO180/1U
kJ/m²
1
Unscented Izod Impact Strength
23°C
ISO180/1U
kJ/m²
1
Suspended wall beam notch impact strength
-30°C
ISO180/1A
kJ/m²
6
Suspended wall beam notch impact strength
23°C
ISO180/1A
kJ/m²
8
Thermal performance
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X5230 BK1G338
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-30到80°C
ISO11359-2
cm/cm/°C
4
Linear coefficient of thermal expansion
TD：-30to80°C
ISO11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
TD:-30到80°C
ISO11359-2
cm/cm/°C
9