PCTG Tritan™ FX100 EASTMAN USA
328
- Unit Price:US$ 3,270 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:26.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜Hydrolysis resistance
- Application Areas:Electrical applications｜Household daily necessities
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D570 | 0.50 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTM D2457 | 161 | |
| refractive index | ASTM D542 | 1.550 | |
| transmittance | ASTM D1003 | 92.0 % | |
| Haze ratio | ASTM D1003 | 0.70 % | |
| Yellowness Index | ASTM D1925 | 0.50 YI | |
| transmittance | 89 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| SurfaceEnergy | ASTM D5946 | 39 dyne/cm | |
| ASTM D5946 | 8 dyne/cm | ||
| ASTM D5946 | 46 dyne/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Abrasion | ASTM D1044 | 23haze % |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | Split8 | ASTM D1938 | 12 kN/m |
| Split9 | ASTM D1938 | 13 kN/m |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tear resistance of pants | ISO 6383-1 | 11.0 N/mm | |
| OTr | ASTM D3985 | 32 cm³·mm/m²/atm/24hr | |
| Water Vapor Transmission Rate | ASTMF1249 | 4.0 g/m²/24hr | |
| ASTMF1249 | 11 g/m²/24hr | ||
| Carbon dioxide transmittance | ASTM D1434 | 150 cm³·mm/m²/atm/24hr | |
| Elmendorf tear strength | ASTM D1922 | 5 N | |
| 6 N | |||
| PPTTearResistance | 42 N | ||
| 56 N | |||
| tear strength | ASTM D1938 | 410 gf | |
| ASTM D1938 | 310 gf | ||
| tensile strength | TD:Yield,250μm | ASTM D882 | 40.0 Mpa |
| MD:Break,250μm | ASTM D882 | 59.0 Mpa | |
| TD:Break,250μm | ASTM D882 | 52.0 Mpa | |
| elongation | MD:Yield,250μm | ASTM D882 | 7.0 % |
| TD:Yield,250μm | ASTM D882 | 7.0 % | |
| MD:Break,250μm | ASTM D882 | 180 % | |
| TD:Break | ASTM D882 | 200 % | |
| Dart impact | ASTM D1709A | 910 g | |
| ASTM D1709A | 880 g | ||
| Tear resistance of pants | ISO 6383-1 | 11.0 N/mm | |
| film thickness | 250 µm | ||
| Thin film puncture strength | ASTM D3763 | 4.60 J | |
| Secant modulus | ASTM D882 | 1500 Mpa | |
| ASTM D882 | 1400 Mpa | ||
| tensile strength | MD:Yield,250μm | ASTM D882 | 41.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 110 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 9E-05 cm/cm/°C | |
| specific heat | DSC | 1700 J/kg/°C | |
| DSC | 1900 J/kg/°C | ||
| DSC | 2200 J/kg/°C | ||
| DSC | 2400 J/kg/°C | ||
| DSC | 2600 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.