Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PCTG FX100 EASTMAN USA
Tritan™
Electrical applications、Household daily necessiti
Chemical resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | EASTMAN USA/FX100 |
|---|---|---|---|
| SurfaceEnergy | Total:23°C,250.0µm | ASTM D5946 | 46 dyne/cm |
| Dispersive:23°C,250.0µm | ASTM D5946 | 39 dyne/cm | |
| Polar:23°C,250mm | ASTM D5946 | 8 dyne/cm |
| film | Test Condition | Test Method | EASTMAN USA/FX100 |
|---|---|---|---|
| Dart impact | -30°C,250µm | ASTM D1709A | 910 g |
| elongation | MD:断裂,250µm | ASTM D882 | 180 % |
| tear strength | MD:23°C,250.0µm | ASTM D1938 | 410 gf |
| Water Vapor Transmission Rate | 23°C,100%RH,250µm | ASTMF1249 | 4.0 g/m²/24hr |
| Thin film puncture strength | 250µm | ASTM D3763 | 4.60 J |
| Carbon dioxide transmittance | 23°C,254.0µm | ASTM D1434 | 150 cm³·mm/m²/atm/24hr |
| Elmendorf tear strength | MD:23°C,250.0µm | ASTM D1922 | 5 N |
| TD:23°C,250.0µm | 6 N | ||
| tensile strength | TD:断裂,250µm | ASTM D882 | 52.0 Mpa |
| elongation | TD:屈服,250µm | ASTM D882 | 7.0 % |
| tensile strength | MD:断裂,250µm | ASTM D882 | 59.0 Mpa |
| film thickness | 250 µm | ||
| tensile strength | MD:屈服,250µm | ASTM D882 | 41.0 Mpa |
| elongation | MD:屈服,250µm | ASTM D882 | 7.0 % |
| Secant modulus | TD:250µm | ASTM D882 | 1400 Mpa |
| MD:250µm | ASTM D882 | 1500 Mpa | |
| PPTTearResistance | MD:23°C,250.0µm | 42 N | |
| tensile strength | TD:屈服,250µm | ASTM D882 | 40.0 Mpa |
| Water Vapor Transmission Rate | 38°C,100%RH,250µm | ASTMF1249 | 11 g/m²/24hr |
| OTr | 23°C,250µm,50%RH | ASTM D3985 | 32 cm³·mm/m²/atm/24hr |
| Dart impact | 23°C,250µm | ASTM D1709A | 880 g |
| PPTTearResistance | TD:23°C,250.0µm | 56 N | |
| tear strength | TD:23°C,250.0µm | ASTM D1938 | 310 gf |
| Tear resistance of pants | MD:250µm | ISO 6383-1 | 11.0 N/mm |
| TD:250µm | ISO 6383-1 | 11.0 N/mm | |
| elongation | TD:断裂 | ASTM D882 | 200 % |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/FX100 |
|---|---|---|---|
| Abrasion | 23°C | ASTM D1044 | 23haze % |
| optical performance | Test Condition | Test Method | EASTMAN USA/FX100 |
|---|---|---|---|
| Yellowness Index | 250mm | ASTM D1925 | 0.50 YI |
| refractive index | ASTM D542 | 1.550 | |
| transmittance | 250µm | ASTM D1003 | 92.0 % |
| 250.0µm，UV | 89 % | ||
| gloss | 60°,250µm | ASTM D2457 | 161 |
| Haze ratio | 250µm | ASTM D1003 | 0.70 % |
| elastomer | Test Condition | Test Method | EASTMAN USA/FX100 |
|---|---|---|---|
| tear strength | 开裂8 | ASTM D1938 | 12 kN/m |
| 开裂9 | ASTM D1938 | 13 kN/m |
| physical property | Test Condition | Test Method | EASTMAN USA/FX100 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr,0.250mm | ASTM D570 | 0.50 % |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/FX100 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23°C,0.250mm | ASTM D696 | 9E-05 cm/cm/°C |
| specific heat | 60°C | DSC | 1700 J/kg/°C |
| 150°C | DSC | 2200 J/kg/°C | |
| 200°C | DSC | 2400 J/kg/°C | |
| 100°C | DSC | 1900 J/kg/°C | |
| melting temperature | 110 °C | ||
| specific heat | 250°C | DSC | 2600 J/kg/°C |