ASA GELOY™ CR7500 BK1041 SABIC INNOVATIVE US
169
- Unit Price:$2139 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:41MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability｜Antistatic｜High mobility
- Application Areas:Automotive Applications｜Electrical applications
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D1238 | 6.3 g/10 min |
| 260°C/5.0 kg | ASTM D1238 | 11 g/10 min | |
| Melt Volume flow Rate | 220°C/10.0 kg | ISO 1133 | 6.00 cm3/10min |
| 260°C/5.0 kg | ISO 1133 | 10.0 cm3/10min | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.80 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.50 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 90.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 88.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 89.0 °C | |
| Vicat Softening Temperature | -- | ASTM D152510 | 98.0 °C |
| -- | ISO 306/B50 | 102 °C | |
| -- | ISO 306/B120 | 105 °C | |
| Ball PressureTest | 98°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 8.4E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 9.5E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 9.5E-5 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 1970 Mpa |
| -- | ISO 527-2/1 | 2040 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 40.0 Mpa |
| 屈服 | ISO 527-2/5 | 43.0 Mpa | |
| 断裂 3 | ASTM D638 | 33.0 Mpa | |
| 断裂 | ISO 527-2/5 | 35.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 3.6 % |
| 屈服 | ISO 527-2/5 | 3.3 % | |
| 断裂 3 | ASTM D638 | 60 % | |
| 断裂 | ISO 527-2/5 | 19 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2170 Mpa |
| -- 5 | ISO 178 | 2060 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 64.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 68.0 Mpa |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 85 到 95 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.040 % | ||
| Suggested Shot Size | 40 到 80 % | ||
| Rear Temperature | 230 到 250 °C | ||
| Middle Temperature | 235 到 255 °C | ||
| Front Temperature | 245 到 260 °C | ||
| Nozzle Temperature | 235 到 255 °C | ||
| Processing (Melt) Temp | 255 到 270 °C | ||
| Mold Temperature | 60 到 85 °C | ||
| Back Pressure | 0.300 到 1.00 Mpa | ||
| Screw Speed | 30 到 80 rpm | ||
| Vent Depth | 0.038 到 0.076 mm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 30.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.