ASA CR7500 BK1041 SABIC INNOVATIVE US
GELOY™
Automotive Applications、Electrical applications
Thermal stability、Antistatic、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CR7500 BK1041 |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 8.4E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 88.0 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 9.5E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 9.5E-5 cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 89.0 °C |
| Vicat Softening Temperature | -- | ISO 306/B50 | 102 °C |
| -- | ASTM D152510 | 98.0 °C | |
| -- | ISO 306/B120 | 105 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 90.0 °C |
| Ball PressureTest | 98°C | IEC 60695-10-2 | 通过 |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/CR7500 BK1041 |
|---|---|---|---|
| Middle Temperature | 235 到 255 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Shot Size | 40 到 80 % | ||
| Drying Temperature | 85 到 95 °C | ||
| Mold Temperature | 60 到 85 °C | ||
| Vent Depth | 0.038 到 0.076 mm | ||
| Suggested Max Moisture | 0.040 % | ||
| Processing (Melt) Temp | 255 到 270 °C | ||
| Rear Temperature | 230 到 250 °C | ||
| Nozzle Temperature | 235 到 255 °C | ||
| Front Temperature | 245 到 260 °C | ||
| Back Pressure | 0.300 到 1.00 Mpa | ||
| Screw Speed | 30 到 80 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/CR7500 BK1041 |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0 kg | ASTM D1238 | 11 g/10 min |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| Melt Volume flow Rate | 220°C/10.0 kg | ISO 1133 | 6.00 cm3/10min |
| Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D1238 | 6.3 g/10 min |
| Melt Volume flow Rate | 260°C/5.0 kg | ISO 1133 | 10.0 cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.80 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.50 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CR7500 BK1041 |
|---|---|---|---|
| Tensile Modulus | -- | ISO 527-2/1 | 2040 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 60 % |
| 断裂 | ISO 527-2/5 | 19 % | |
| Tensile Strength | 断裂 | ISO 527-2/5 | 35.0 Mpa |
| 屈服 3 | ASTM D638 | 40.0 Mpa | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2170 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 1970 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/5 | 3.3 % |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 68.0 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 3.6 % |
| Flexural Stress | -- 5, 6 | ISO 178 | 64.0 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 2060 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/5 | 43.0 Mpa |
| 断裂 3 | ASTM D638 | 33.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CR7500 BK1041 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 30.0 J |