PBT Cristin® S600F20 BK851 DUPONT USA
136
Unit Price:$4960 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity｜Good dimensional stabilit｜Good resistance to chemic
- Application Areas:Electronic and electrical｜Automotive Applications｜Industrial applications｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Moisture Absorption | -，23C/59RH | ISO 62 | 0.2 % |
| -，Sat/23C | ISO 62 | 0.40 % | |
| Modeling Shrinkage | -，Across Flow | ISO 294-4 | 1.6 % |
| -，Flow | ISO 294-4 | 1.7 % | |
| Density / Specific Gravity | ISO 1183 | 1.31 g/cm | |
| MediumDensity | 1.11 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| SpecificHeatCapacityofMelt | 2110 J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 W/m/K | ||
| Density / Specific Gravity | ISO1183 | 1.31 g/cm³ | |
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 19 g/10min |
| Modeling Shrinkage | TD | ISO294-4 | 1.6 % |
| MD | ISO294-4 | 1.7 % | |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 0.40 % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % | |
| Viscosity number | ISO307 | 130 cm³/g |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melting temperature | ISO 3146 | 225 ℃ | |
| Coefficient of Linear Thermal Expansion | 平行流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1, -2 | 0.00013 cm/cm/°C |
| 垂直流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1, -2 | 0.00013 cm/cm/°C | |
| Heat Deflection Temperature | -，0.45 Mpa，未退火 | ISO 75B-1, -2 | 180 ℃ |
| -，1.8 Mpa，未退火 | ISO 75B-1, -2 | 60 ℃ | |
| Flame retardant grade | 1.50 mm | UL94 HB | |
| 3.00 mm | UL94 HB | ||
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 8E-05 cm/cm/°C |
| MD：55to160°C | ISO11359-2 | 1.9E-04 cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.2E-04 cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 2E-04 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 115 °C |
| 0.45MPa,退火 | ISO75-2/B | 180 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 50.0 °C | |
| 1.8MPa,退火 | ISO75-2/A | 60.0 °C | |
| Glass Transition Temperature | ISO11357-2 | 55.0 °C | |
| Vicat Softening Temperature | ISO306/B50 | 175 °C | |
| Melting Temperature | ISO11357-3 | 225 °C | |
| PeakCrystallizationTemperature2 | ISO11357-3 | 192 °C | |
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Additional | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Odor3 | VDA270 | 3.00 | |
| ThermalDesorptionAnalysisofOrganicEmissions4 | VDA278 | 1.00 µg/g |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | HB |
| 1.5mm | UL94 | HB | |
| 0.75mm | IEC60695-11-10,-20 | HB | |
| 1.5mm | IEC60695-11-10,-20 | HB | |
| Oxygen Index | ISO4589-2 | 22 % | |
| FMVSS Flammability | FMVSS302 | SE | |
| Fogging-G-value | condensate | ISO6452 | 0.0 g |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -，23 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| -，-30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4 KJ/m | |
| -，23 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4.5 KJ/m | |
| Notched Impact Strength | 23 ℃, Type 1, Notch A | ISO 180 | 4 KJ/m |
| Tensile Stress (Yield) | 23 ℃, 50 mm/min | ISO 527-1, -2 | 58 MPa |
| Tensile Strain (Yield) | 23 ℃, 50 mm/min | ISO 527-1, -2 | 7.6 % |
| Tensile Strain (Break) | 23 ℃, 50 mm/min | ISO 527-1, -2 | 40 % |
| Tensile Creep Modulus | -，1000h | ISO 899-1 | 1800 MPa |
| Tensile Modulus | 23 ℃, 1.0 mm/min | ISO 527-1, -2 | 2600 MPa |
| Flexural Strength | ISO 178 | 85 MPa | |
| Charpy Notched Impact Strength | -，-30 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Nominal Tensile Strain at Break | ISO527-2 | 40 % | |
| Tensile Creep Modulus | 1hr | ISO899-1 | 2600 Mpa |
| 1000hr | ISO899-1 | 1800 Mpa | |
| Flexural Modulus | ISO178 | 2200 Mpa | |
| Flexural Stress | ISO178 | 85.0 Mpa | |
| Tensile Modulus | ISO527-2 | 2500 Mpa | |
| Tensile Stress | 屈服 | ISO527-2 | 58.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2 | 5.0 % |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor? | 100Hz | IEC60250 | 7.9E-04 |
| 1MHz | IEC60250 | 0.020 | |
| Comparative Tracking Index | IEC60112 | 400 V | |
| Surface Resistivity | IEC60093 | 1E+12 ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | IEC60243-1 | 26 KV/mm | |
| Relative Permittivity | 100Hz | IEC60250 | 3.60 |
| 1MHz | IEC60250 | 3.20 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.0 kJ/m² |
| 23°C | ISO179/1eA | 5.0 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | ISO179/1eU | NoBreak | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 4.5 kJ/m² |
| Notched Izod impact strength | 23°C | ISO180/1U | NoBreak |
| Other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Oxygen Index | ISO 4589-1, -2 | 22 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.