Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S600F20 BK851 DUPONT USA
Cristin®
Electronic and electrical、Automotive Applications、Industrial applications、Automotive Applications
Medium viscosity、Good dimensional stabilit、Good resistance to chemic
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Glass Transition Temperature | ISO11357-2 | 55.0 °C | |
| Heat Deflection Temperature | 1.8MPa,退火 | ISO75-2/A | 60.0 °C |
| Linear thermal expansion coefficient | TD：-- | ISO11359-2 | 1.2E-04 cm/cm/°C |
| TD：55to160°C | 2E-04 cm/cm/°C | ||
| ISO11357-3 | 192 °C | ||
| Melting temperature | ISO 3146 | 225 ℃ | |
| Vicat Softening Temperature | ISO306/B50 | 175 °C | |
| Heat Deflection Temperature | 0.45MPa,退火 | ISO75-2/B | 180 °C |
| Linear thermal expansion coefficient | TD：-40to23°C | ISO11359-2 | 9E-05 cm/cm/°C |
| Coefficient of Linear Thermal Expansion | 平行流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1, -2 | 0.00013 cm/cm/°C |
| Flame retardant grade | 1.50 mm | UL94 HB | |
| Heat Deflection Temperature | -，0.45 Mpa，未退火 | ISO 75B-1, -2 | 180 ℃ |
| 0.45MPa,未退火 | ISO75-2/B | 115 °C | |
| -，1.8 Mpa，未退火 | ISO 75B-1, -2 | 60 ℃ | |
| 1.8MPa,未退火 | ISO75-2/A | 50.0 °C | |
| Coefficient of Linear Thermal Expansion | 垂直流动方向，23 to 55°C (73 to 130°F) | ISO 11359-1, -2 | 0.00013 cm/cm/°C |
| Linear thermal expansion coefficient | MD：55to160°C | ISO11359-2 | 1.9E-04 cm/cm/°C |
| MD：-40to23°C | 8E-05 cm/cm/°C | ||
| Melting Temperature | ISO11357-3 | 225 °C | |
| Flame retardant grade | 3.00 mm | UL94 HB | |
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Additional | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| VDA278 | 1.00 µg/g | ||
| VDA270 | 3.00 |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Tensile Modulus | 23 ℃, 1.0 mm/min | ISO 527-1, -2 | 2600 MPa |
| Tensile Strain (Break) | 23 ℃, 50 mm/min | 40 % | |
| Tensile Strain | 屈服 | ISO527-2 | 5.0 % |
| Charpy Notched Impact Strength | -，-30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 4 KJ/m |
| Tensile Stress | 屈服 | ISO527-2 | 58.0 Mpa |
| Tensile Strain (Yield) | 23 ℃, 50 mm/min | ISO 527-1, -2 | 7.6 % |
| Flexural Modulus | ISO178 | 2200 Mpa | |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 1800 Mpa |
| Flexural Strength | ISO 178 | 85 MPa | |
| Tensile Stress (Yield) | 23 ℃, 50 mm/min | ISO 527-1, -2 | 58 MPa |
| Notched Impact Strength | 23 ℃, Type 1, Notch A | ISO 180 | 4 KJ/m |
| Charpy Notched Impact Strength | -，-30 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| -，23 ℃, Type 1, Edgewise, Notch A | 4.5 KJ/m | ||
| Nominal Tensile Strain at Break | ISO527-2 | 40 % | |
| Tensile Creep Modulus | -，1000h | ISO 899-1 | 1800 MPa |
| Flexural Stress | ISO178 | 85.0 Mpa | |
| Charpy Notched Impact Strength | -，23 ℃, Type 1, Edgewise | ISO 179 | No Break KJ/m |
| Tensile Creep Modulus | 1hr | ISO899-1 | 2600 Mpa |
| Tensile Modulus | ISO527-2 | 2500 Mpa |
| Physical | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Viscosity number | ISO307 | 130 cm³/g | |
| Modeling Shrinkage | -，Across Flow | ISO 294-4 | 1.6 % |
| ThermalConductivityofMelt | 0.21 W/m/K | ||
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 0.40 % |
| MediumDensity | 1.11 g/cm³ | ||
| Moisture Absorption | -，23C/59RH | ISO 62 | 0.2 % |
| Ejection Temperature | 170 °C | ||
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 19 g/10min |
| Moisture Absorption | -，Sat/23C | ISO 62 | 0.40 % |
| Modeling Shrinkage | -，Flow | ISO 294-4 | 1.7 % |
| Density / Specific Gravity | ISO 1183 | 1.31 g/cm | |
| ISO1183 | 1.31 g/cm³ | ||
| SpecificHeatCapacityofMelt | 2110 J/kg/°C | ||
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % |
| Modeling Shrinkage | TD | ISO294-4 | 1.6 % |
| MD | 1.7 % |
| Other | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Oxygen Index | ISO 4589-1, -2 | 22 % |
| Impact Properties | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Notched Izod impact strength | 23°C | ISO180/1U | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.0 kJ/m² |
| 23°C | 5.0 kJ/m² | ||
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | NoBreak | ||
| Notched Izod Impact Strength | ISO180/1A | 4.5 kJ/m² |
| Flammability | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Flame Rating | 0.75mm | IEC60695-11-10,-20 | HB |
| 1.5mm | HB | ||
| 0.75mm | UL94 | HB | |
| Fogging-G-value | condensate | ISO6452 | 0.0 g |
| Flame Rating | 1.5mm | UL94 | HB |
| Oxygen Index | ISO4589-2 | 22 % | |
| FMVSS Flammability | FMVSS302 | SE |
| Electrical Properties | Test Condition | Test Method | DUPONT USA/S600F20 BK851 |
|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.60 |
| Dielectric Strength | IEC60243-1 | 26 KV/mm | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 400 V | |
| Surface Resistivity | IEC60093 | 1E+12 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 3.20 |
| Dissipation Factor? | 100Hz | 7.9E-04 |