PBT Cristin® S600F10 DUPONT USA
147
Unit Price:$3240 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 119.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high viscosity
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | TD | ISO294-4 | 1.7 | % |
| MD | ISO294-4 | 1.7 | % | |
| -，Across Flow | ISO 294-4 | 1.6 | % | |
| -，Flow | ISO 294-4 | 1.7 | % | |
| 吸水率 | -，23C/59RH | ISO 62 | % | |
| -，Sat/23C | ISO 62 | % | ||
| 饱和,23°C,2.00mm | ISO62 | 0.50 | % | |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MeltDensity | 1.11 | g/cm³ | ||
| 顶出温度 | 170 | °C | ||
| SpecificHeatCapacityofMelt | 2100 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 | W/m/K | ||
| 熔体质量流动速率 | 250°C/2.16kg | ISO1133 | 10 | g/10min |
| 密度 | ISO1183 | 1.30 | g/cm³ | |
| ISO 1183 | g/cm |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 4.0 | kJ/m² |
| 23°C | ISO179/1eA | 5.0 | kJ/m² | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² | |
| 悬臂梁无缺口冲击强度 | -30°C | ISO180/1U | 130 | kJ/m² |
| 23°C | ISO180/1U | NoBreak | ||
| TensileCreepModulus | 1hr | ISO899-1 | 2300 | Mpa |
| 简支梁缺口冲击强度 | -，-30 ℃, Type 1, Edgewise, Notch A | ISO 179 | KJ/m | |
| -，23 ℃, Type 1, Edgewise, Notch A | ISO 179 | KJ/m | ||
| 标称拉伸断裂应变 | ISO527-2 | >50 | % | |
| Charpy 非缺口冲击强度 | -，-30℃, Type 1, Edgewise | ISO 179 | KJ/m | |
| -，23℃, Type 1, Edgewise | ISO 179 | KJ/m | ||
| 非缺口冲击强度 | 23 ℃, Type 1 | ISO 180 | KJ/m | |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| 断裂点拉伸应变 | 23 ℃, 50 mm/min | ISO 527-1, -2 | % | |
| 屈服点拉伸应力 | 23℃ | ISO 527-1, -2 | 57 | Mpa |
| 屈服点拉伸应变 | 23℃ | ISO 527-1, -2 | % | |
| 断裂点名义拉伸应变 | 23℃ | ISO 527-1, -2 | % | |
| 缺口冲击强度 | 23 ℃, Type 1, Notch A | ISO 180 | KJ/m | |
| 拉伸蠕变模量 | -，1h | ISO 899-1 | 2600 | Mpa |
| -，1000h | ISO 899-1 | 1800 | Mpa | |
| 1000hr | ISO899-1 | 1800 | Mpa | |
| 拉伸模量 | 23℃ | ISO 527-1, -2 | 2700 | Mpa |
| ISO527-2 | 2600 | Mpa | ||
| 拉伸强度 | 屈服 | ISO527-2 | 57.0 | Mpa |
| 伸长率 | 屈服 | ISO527-2 | 4.0 | % |
| 弯曲模量 | ISO178 | 2300 | Mpa | |
| 弯曲强度 | ISO178 | 85.0 | Mpa | |
| 23℃ | ISO 178 | 85 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 维卡软化点 | ISO306/B50 | 175 | °C | |
| 阻燃等级 | 0.750 mm | UL 94 | HB | |
| 1.50 mm | UL94 | HB | ||
| 3.00 mm | UL 94 | HB | ||
| 线性热膨胀系数 | 平行流动方向，23 to 55℃ (73 to 130°F) | cm/cm/℃ | ||
| 垂直流动方向，23 to 55℃ (73 to 130°F) | cm/cm/℃ | |||
| MD：-40to23°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.9E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 2E-04 | cm/cm/°C | |
| MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| 熔融温度 | ISO 3146 | 225 | ℃ | |
| ISO11357-3 | 224 | °C | ||
| 热变形温度 | -，0.45 Mpa，未退火 | 160 | ℃ | |
| -，1.8Mpa，未退火 | ISO 75A-1, -2 | ℃ | ||
| 0.45MPa,未退火 | ISO75-2/B | 115 | °C | |
| 0.45MPa,退火 | ISO75-2/B | 180 | °C | |
| 1.8MPa,未退火 | ISO75-2/A | 50.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 60.0 | °C | |
| 玻璃转化温度 | ISO11357-2 | 55.0 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相对电容率 | 100Hz | IEC60250 | 3.60 | |
| 1MHz | IEC60250 | 3.20 | ||
| 漏电起痕指数 | IEC60112 | 400 | V | |
| 介电强度 | -- | IEC60243-1 | 26 | KV/mm |
| 1.00mm3 | IEC60243-1 | 26 | KV/mm | |
| 2.00mm4 | IEC60243-1 | 15 | KV/mm | |
| 耗散因数 | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 0.020 | ||
| 表面电阻率 | IEC60093 | 1E+15 | ohms | |
| 体积电阻率 | IEC60093 | >1.0E+15 | ohms·cm |
| 其它性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 极限氧指数 | 22 | % |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| 极限氧指数 | ISO4589-2 | 22 | % | |
| FMVSS可燃性 | FMVSS302 | SE |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 145 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.