Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S600F10 DUPONT USA
Cristin®
Electronic and electrical、Automotive Applications
high viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/DUPONT USA/S600F10
density
ISO 1183
g/cm
density
ISO1183
g/cm³
1
Melt mass flow rate
250°C/2.16kg
ISO1133
g/10min
1
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
1
Shrinkage rate
-，Across Flow
ISO 294-4
%
1
Shrinkage rate
-，Flow
ISO 294-4
%
1
Water absorption rate
-，23C/59RH
ISO 62
%
Water absorption rate
-，Sat/23C
ISO 62
%
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
0
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/S600F10
Charpy non notched impact strength
-，-30℃, Type 1, Edgewise
ISO 179
KJ/m
Charpy non notched impact strength
-，23℃, Type 1, Edgewise
ISO 179
KJ/m
TensileCreepModule
1hr
ISO899-1
Mpa
2
Nominal tensile fracture strain
ISO527-2
%
>
Fracture point tensile strain
23 ℃, 50 mm/min
ISO 527-1, -2
%
Nominal tensile strain at the fracture point
23℃
ISO 527-1, -2
%
Non notched impact strength
23 ℃, Type 1
ISO 180
KJ/m
Impact strength of simply supported beam gap
-，-30 ℃, Type 1, Edgewise, Notch A
ISO 179
KJ/m
Impact strength of simply supported beam gap
-，23 ℃, Type 1, Edgewise, Notch A
ISO 179
KJ/m
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
4
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
5
Tensile modulus
23℃
ISO 527-1, -2
Mpa
2
Tensile modulus
ISO527-2
Mpa
2
tensile strength
屈服
ISO527-2
Mpa
5
Tensile creep modulus
-，1h
ISO 899-1
Mpa
2
Tensile creep modulus
-，1000h
ISO 899-1
Mpa
1
Tensile creep modulus
1000hr
ISO899-1
Mpa
1
Yield point tensile strain
23℃
ISO 527-1, -2
%
Yield point tensile stress
23℃
ISO 527-1, -2
Mpa
5
Gap impact strength
23 ℃, Type 1, Notch A
ISO 180
KJ/m
elongation
屈服
ISO527-2
%
4
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
8
bending strength
23℃
ISO 178
Mpa
8
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
5
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
5
Cantilever beam without notch impact strength
-30°C
ISO180/1U
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/S600F10
Glass transition temperature
ISO11357-2
°C
5
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
0.45MPa,退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
5
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
6
Hot deformation temperature
-，1.8Mpa，未退火
ISO 75A-1, -2
℃
Melting temperature
ISO11357-3
°C
2
Melting temperature
ISO 3146
℃
2
vicat softening point
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD：--
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：-40to23°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
MD：55to160°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：--
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40to23°C
ISO11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：55to160°C
ISO11359-2
cm/cm/°C
2
Electrical performance
Test Condition
Test Method
Unit
PBT/DUPONT USA/S600F10
Surface resistivity
IEC60093
ohms
1
Dielectric strength
--
IEC60243-1
KV/mm
2
Dielectric strength
1.00mm3
IEC60243-1
KV/mm
2
Dielectric strength
2.00mm4
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
4
Volume resistivity
IEC60093
ohms·cm
>
flammability
Test Condition
Test Method
Unit
PBT/DUPONT USA/S600F10
Extreme Oxygen Index
ISO4589-2
%
2
Supplementary Information
Test Condition
Test Method
Unit
PBT/DUPONT USA/S600F10
EmissionofOrganicCompounds
VDA277
µgC/g
1