LCP VECTRA® A130D-3BK-VD3006 CELANESE USA
165
- Unit Price:$6209 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜Thermal stability｜Chemical resistance
- Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 0.40 % |
| 流量 | ISO 294-4 | 0.20 % | |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 250 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 235 °C | |
| 8.0 MPa, 未退火 | ISO 75-2/C | 190 °C | |
| Vicat Softening Temperature | ISO 306/B50 | 160 °C | |
| Melting Temperature | ISO 11357-3 | 280 °C | |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 6.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 2.3E-5 cm/cm/°C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Oxygen Index | ISO 4589-2 | 45 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1A | 15000 Mpa | |
| Tensile Stress | 断裂 | ISO 527-2/1A/5 | 190 Mpa |
| Tensile Strain | 断裂 | ISO 527-2/1A/5 | 2.1 % |
| Tensile Creep Modulus | 1 hr | ISO 899-1 | 12600 Mpa |
| 1000 hr | ISO 899-1 | 10900 Mpa | |
| Flexural Modulus | 23°C | ISO 178 | 14500 Mpa |
| Flexural Stress | 23°C | ISO 178 | 280 Mpa |
| Compressive Modulus | ISO 604 | 14500 Mpa | |
| Compressive Stress | 1% 应变 | ISO 604 | 100 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume Resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Dielectric Strength | IEC 60243-1 | 31 KV/mm | |
| Relative Permittivity | 100 Hz | IEC 60250 | 4.20 |
| 1 MHz | IEC 60250 | 3.70 | |
| Dissipation Factor? | 100 Hz | IEC 60250 | 0.016 |
| 1 MHz | IEC 60250 | 0.018 | |
| Arc Resistance | 内部方法 | 140 sec | |
| Comparative Tracking Index | IEC 60112 | 175 V |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 150 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Max Moisture | 0.010 % | ||
| Hopper Temperature | 20 到 30 °C | ||
| Rear Temperature | 270 到 280 °C | ||
| Middle Temperature | 275 到 285 °C | ||
| Front Temperature | 280 到 290 °C | ||
| Nozzle Temperature | 290 到 300 °C | ||
| Processing (Melt) Temp | 285 到 295 °C | ||
| Mold Temperature | 80 到 120 °C | ||
| Injection Rate | 快速 | ||
| Back Pressure | < 3.00 Mpa |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | M 计秤 | ISO 2039-2 | 85 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Notched Izod impact strength | 23°C | ISO 180/1U | 29 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.