LCP A130D-3BK-VD3006 CELANESE USA
VECTRA®
Electrical field、Electronic field、Household appliances、Household appliances
Flame retardant、Glass fiber reinforced、Thermal stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Vicat Softening Temperature | ISO 306/B50 | 160 °C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 250 °C |
| Melting Temperature | ISO 11357-3 | 280 °C | |
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 235 °C |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 6.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 2.3E-5 cm/cm/°C | |
| Heat Deflection Temperature | 8.0 MPa, 未退火 | ISO 75-2/C | 190 °C |
| Hardness | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Rockwell Hardness | M 计秤 | ISO 2039-2 | 85 |
| Injection | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Injection Rate | 快速 | ||
| Suggested Max Moisture | 0.010 % | ||
| Middle Temperature | 275 到 285 °C | ||
| Processing (Melt) Temp | 285 到 295 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Rear Temperature | 270 到 280 °C | ||
| Nozzle Temperature | 290 到 300 °C | ||
| Drying Temperature | 150 °C | ||
| Front Temperature | 280 到 290 °C | ||
| Hopper Temperature | 20 到 30 °C | ||
| Back Pressure | < 3.00 Mpa | ||
| Mold Temperature | 80 到 120 °C |
| Physical | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 0.40 % |
| 流量 | ISO 294-4 | 0.20 % |
| Mechanical Properties | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Flexural Stress | 23°C | ISO 178 | 280 Mpa |
| Tensile Strain | 断裂 | ISO 527-2/1A/5 | 2.1 % |
| Flexural Modulus | 23°C | ISO 178 | 14500 Mpa |
| Tensile Modulus | ISO 527-2/1A | 15000 Mpa | |
| Tensile Creep Modulus | 1 hr | ISO 899-1 | 12600 Mpa |
| Compressive Modulus | ISO 604 | 14500 Mpa | |
| Tensile Creep Modulus | 1000 hr | ISO 899-1 | 10900 Mpa |
| Tensile Stress | 断裂 | ISO 527-2/1A/5 | 190 Mpa |
| Compressive Stress | 1% 应变 | ISO 604 | 100 Mpa |
| Impact Properties | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Notched Izod impact strength | 23°C | ISO 180/1U | 29 kJ/m² |
| Flammability | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Oxygen Index | ISO 4589-2 | 45 % | |
| UL flame retardant rating | UL 94 | V-0 |
| Electrical Properties | Test Condition | Test Method | CELANESE USA/A130D-3BK-VD3006 |
|---|---|---|---|
| Arc Resistance | 内部方法 | 140 sec | |
| Relative Permittivity | 100 Hz | IEC 60250 | 4.20 |
| Dissipation Factor? | 100 Hz | IEC 60250 | 0.016 |
| Relative Permittivity | 1 MHz | IEC 60250 | 3.70 |
| Dielectric Strength | IEC 60243-1 | 31 KV/mm | |
| Dissipation Factor? | 1 MHz | IEC 60250 | 0.018 |
| Volume Resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC 60112 | 175 V | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms |