PC/ABS CYCOLAC™ CX2244ME GY5D096 SABIC INNOVATIVE US
135
Unit Price:$4305 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc｜High sliding
- Application Areas:Electronic and electrical｜Automotive components
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 18 g/10min |
| Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 15.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.60 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.20 % |
| 平衡,23°C,50%RH | ISO62 | 0.10 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 89.0 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 93.0 °C | |
| Vicat Softening Temperature | ASTMD152510 | 110 °C | |
| -- | ISO306/B50 | 110 °C | |
| -- | ISO306/B120 | 113 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C | |
| RTIElec | UL746 | 90.0 °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 °C | |
| RTIStr | UL746 | 90.0 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | 5VB |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 800 °C |
| Flame Rating | 0.75mm | UL94 | V-0 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Elongation | 断裂 | ASTMD638 | 100 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 90 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2500 Mpa |
| ISO178 | 2500 Mpa | ||
| Flexural Strength | ISO178 | 96.0 Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 104 Mpa | |
| Tensile Modulus | ASTMD638 | 2600 Mpa | |
| ISO527-2/1 | 2600 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 65.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 65.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 50.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.1 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.0 % |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC 3 |
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 kJ/m² |
| 23°C | ISO179/1eA | 40 kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| 23°C | ISO180/1A | 40 kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 65.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.