Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CX2244ME GY5D096 SABIC INNOVATIVE US
CYCOLAC™
Electronic and electrical、Automotive components
Low temperature resistanc、High sliding
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX2244ME GY5D096 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C |
| RTIElec | UL746 | 90.0 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 89.0 °C |
| RTIStr | UL746 | 90.0 °C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 113 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 93.0 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 110 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| Vicat Softening Temperature | ASTMD152510 | 110 °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX2244ME GY5D096 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2500 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 50.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 100 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 90 % |
| Tensile Modulus | ISO527-2/1 | 2600 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 65.0 Mpa |
| Flexural Modulus | ISO178 | 2500 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 104 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.1 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 65.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.0 % |
| Flexural Strength | ISO178 | 96.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2600 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/CX2244ME GY5D096 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.10 % |
| Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 15.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.60 % |
| Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 18 g/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.20 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX2244ME GY5D096 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 65.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 40 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 40 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/CX2244ME GY5D096 |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | V-0 |
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 800 °C |
| Flame Rating | 1.5mm | UL94 | 5VB |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/CX2244ME GY5D096 |
|---|---|---|---|
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |