PC/ABS CYCOLAC™ C1200-100 SABIC INNOVATIVE US
172
Unit Price:$3042 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 87.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:High impact resistance｜heat-resisting
- Application Areas:Electrical field｜Electronic field｜Automotive interior parts
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 19 g/10min |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 24.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 129 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 130 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 113 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 110 °C | |
| Vicat Softening Temperature | ISO306/B50 | 130 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| RTIElec | UL746 | 105 °C | |
| Evolution Calendar intelligent importer | UL746 | 80.0 °C | |
| RTIStr | UL746 | 105 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.2mm | UL94 | HB |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTMD638 | 2280 Mpa | |
| ISO527-2/1 | 2370 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 57.2 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.8 % |
| Tensile Elongation | 断裂 | ASTMD638 | 150 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 110 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2340 Mpa |
| ISO178 | 2250 Mpa | ||
| Flexural Stress | ISO178 | 86.0 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 88.3 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 1 |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 34 kJ/m² |
| 23°C | ISO180/1A | 49 kJ/m² | |
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 54.2 J |
| 23°C,TotalEnergy | ASTMD3763 | 54.2 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.