Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C1200-100 SABIC INNOVATIVE US
CYCOLAC™
Electrical field、Electronic field、Automotive interior parts
High impact resistance、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200-100 |
|---|---|---|---|
| RTIElec | UL746 | 105 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 129 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 130 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 113 °C | |
| RTIStr | UL746 | 105 °C | |
| Vicat Softening Temperature | ISO306/B50 | 130 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 110 °C |
| Evolution Calendar intelligent importer | UL746 | 80.0 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/C1200-100 |
|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 24.0 cm3/10min |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 19 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200-100 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2340 Mpa |
| ISO178 | 2250 Mpa | ||
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 88.3 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 150 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 110 % |
| 屈服 | ISO527-2/50 | 4.8 % | |
| Tensile Modulus | ISO527-2/1 | 2370 Mpa | |
| Flexural Stress | ISO178 | 86.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2280 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 57.2 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200-100 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 34 kJ/m² |
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 54.2 J |
| 23°C,TotalEnergy | ASTMD3763 | 54.2 J | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 49 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/C1200-100 |
|---|---|---|---|
| Flame Rating | 1.2mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200-100 |
|---|---|---|---|
| High Amp Arc Ignition | HAI | UL746 | PLC 1 |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |