PC/ABS CYCOLAC™ C1200HF-111 SABIC INNOVATIVE US
143
Unit Price:$2505 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:High impact resistance｜heat-resisting
- Application Areas:Electrical field｜Electronic field｜Automotive interior parts
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0 kg | ASTM D1238 | 19 g/10 min |
| Melt Volume flow Rate | 265°C/5.0 kg | ISO 1133 | 24.0 cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 129 °C |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Bf | 130 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 112 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Af | 110 °C | |
| Vicat Softening Temperature | ISO 306/B50 | 130 °C | |
| Coefficient of Linear Thermal Expansion (Flow) | -40 到 40°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| RTI Elec | UL 746 | 105 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 105 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.2 mm | UL 94 | HB |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2270 Mpa |
| -- | ISO 527-2/1 | 2360 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 57.0 Mpa |
| 屈服 | ISO 527-2/50 | 55.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.0 % |
| 屈服 | ISO 527-2/50 | 4.8 % | |
| 断裂 3 | ASTM D638 | 150 % | |
| 断裂 | ISO 527-2/50 | 110 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2340 Mpa |
| -- | ISO 178 | 2250 Mpa | |
| Flexural Stress | -- | ISO 178 | 86.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 88.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 2 | |
| High Amp Arc Ignition | UL 746 | PLC 1 | |
| Hot-wire Ignition | UL 746 | PLC 3 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 100 到 110 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 30 到 80 % | ||
| Hopper Temperature | 60 到 80 °C | ||
| Rear Temperature | 250 到 290 °C | ||
| Middle Temperature | 255 到 295 °C | ||
| Front Temperature | 260 到 300 °C | ||
| Nozzle Temperature | 275 到 300 °C | ||
| Processing (Melt) Temp | 275 到 300 °C | ||
| Mold Temperature | 60 到 90 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.038 到 0.076 mm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | -30°C, Total Energy | ASTM D3763 | 54.0 J |
| 23°C, Total Energy | ASTM D3763 | 54.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.