Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C1200HF-111 SABIC INNOVATIVE US
CYCOLAC™
Electrical field、Electronic field、Automotive interior parts
High impact resistance、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200HF-111 |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Bf | 130 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Af | 110 °C | |
| RTI | UL 746 | 105 °C | |
| Vicat Softening Temperature | ISO 306/B50 | 130 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Elec | 105 °C | ||
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 112 °C |
| 0.45 MPa, 未退火, 3.20 mm | 129 °C | ||
| Coefficient of Linear Thermal Expansion (Flow) | -40 到 40°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/C1200HF-111 |
|---|---|---|---|
| Middle Temperature | 255 到 295 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Shot Size | 30 到 80 % | ||
| Drying Temperature | 100 到 110 °C | ||
| Mold Temperature | 60 到 90 °C | ||
| Vent Depth | 0.038 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 275 到 300 °C | ||
| Rear Temperature | 250 到 290 °C | ||
| Nozzle Temperature | 275 到 300 °C | ||
| Front Temperature | 260 到 300 °C | ||
| Hopper Temperature | 60 到 80 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/C1200HF-111 |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0 kg | ASTM D1238 | 19 g/10 min |
| Melt Volume flow Rate | 265°C/5.0 kg | ISO 1133 | 24.0 cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200HF-111 |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2270 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| Flexural Stress | -- | ISO 178 | 86.0 Mpa |
| Tensile Modulus | ISO 527-2/1 | 2360 Mpa | |
| Tensile Elongation | 断裂 3 | ASTM D638 | 150 % |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 88.0 Mpa |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.0 % |
| Flexural Modulus | -- | ISO 178 | 2250 Mpa |
| Tensile Strength | 屈服 3 | ASTM D638 | 57.0 Mpa |
| Tensile Elongation | 屈服 | ISO 527-2/50 | 4.8 % |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2340 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 110 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200HF-111 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 54.0 J |
| -30°C, Total Energy | 54.0 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/C1200HF-111 |
|---|---|---|---|
| UL flame retardant rating | 1.2 mm | UL 94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/C1200HF-111 |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 3 | |
| Comparative Tracking Index | PLC 2 | ||
| High Amp Arc Ignition | PLC 1 |