PC LEXAN™ ML3729-111H SABIC INNOVATIVE US
93
Unit Price:$3546 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High toughness｜transparent
- Application Areas:Automotive components｜Electronic and electrical
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.090 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 39 g/10min |
| Melt Volume flow Rate | 250°C/1.2kg | ISO1133 | 6.00 cm3/10min |
| 300°C/1.2kg | ISO1133 | 36.0 cm3/10min | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| TD：3.20mm | 内部方法 | 0.50to0.70 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.27 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 7.8E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7.8E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 135 °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 133 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 125 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 121 °C | |
| Vicat Softening Temperature | ASTMD152510 | 140 °C | |
| -- | ISO306/B50 | 139 °C | |
| -- | ISO306/B120 | 140 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTMD638 | 2410 Mpa | |
| ISO527-2/1 | 2300 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 62.6 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 60.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 6.0 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 5.7 % |
| Tensile Elongation | 断裂 | ASTMD638 | 110 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 110 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2410 Mpa |
| ISO178 | 2300 Mpa | ||
| Flexural Strength | ISO178 | 85.0 Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 102 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 12 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 66.2 J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.0 kJ/m² |
| 23°C | ISO179/1eA | 12 kJ/m² | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 4.0 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.