Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML3729-111H SABIC INNOVATIVE US
LEXAN™
Automotive components、Electronic and electrical
High toughness、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML3729-111H |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7.8E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 121 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 139 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 135 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7.8E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 133 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 125 °C | |
| Vicat Softening Temperature | ASTMD152510 | 140 °C | |
| -- | ISO306/B120 | 140 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/ML3729-111H |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.090 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 39 g/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 36.0 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.27 % |
| Melt Volume flow Rate | 250°C/1.2kg | ISO1133 | 6.00 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML3729-111H |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2410 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 110 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 110 % |
| Tensile Modulus | ISO527-2/1 | 2300 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 62.6 Mpa |
| Flexural Modulus | ISO178 | 2300 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 102 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 6.0 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 60.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 5.7 % |
| Flexural Strength | ISO178 | 85.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2410 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML3729-111H |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 4.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 5.0 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 66.2 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 12 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 12 kJ/m² |