Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability｜Middle flow
- Application Areas:Electrical applications｜Lighting applications｜Automotive Applications
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific Volume | ASTMD792 | 0.835 cm³/g | |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 2.0 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 2.00 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.80到1.0 % |
| 24hr | ASTMD570 | 0.19 % | |
| Saturation ,23℃ | ISO62 | 0.16 % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.35 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 149 °C | |
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 150 °C | |
| Flow:-40 to 40°C | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C | |
| Flow:-40 to 95°C | ASTME831 | 8.1E-05 cm/cm/°C | |
| Flow:-40 to 40°C | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C | |
| Specific Heat | ASTMC351 | 1260 J/kg/°C | |
| Thermal Conductivity | ASTMC177 | 0.21 W/m/K | |
| RTIElec | UL746 | 130 °C | |
| Evolution Calendar intelligent importer | UL746 | 130 °C | |
| RTI | UL746 | 130 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.600 | |
| Transmittance | 2540µm | ASTMD1003 | 85.0 % |
| Haze | 2540µm | ASTMD1003 | 1.0 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.47mm | UL94 | HB |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 50.0mm Span | ASTMD790 | 2330 Mpa | |
| --7 | ISO178 | 2070 Mpa | |
| --8 | ISO178 | 66.0 Mpa | |
| Yield,50.0mm Span | ASTMD790 | 97.2 Mpa | |
| --1 | ASTMD638 | 2080 Mpa | |
| Yield | ASTMD638 | 65.5 Mpa | |
| yield | ISO527-2/50 | 68.0 Mpa | |
| Break | ASTMD638 | 77.9 Mpa | |
| fracture | ISO527-2/50 | 68.0 Mpa | |
| Yield | ASTMD638 | 8.0 % | |
| yield | ISO527-2/50 | 7.0 % | |
| Break | ASTMD638 | 78 % | |
| fracture | ISO527-2/50 | 100 % |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor? | 50Hz | ASTMD150 | 1.6E-03 |
| 60Hz | ASTMD150 | 1.6E-03 | |
| 100Hz | ASTMD150 | 0.026 | |
| Arc Resistance | ASTMD495 | PLC6 | |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |
| High Amp Arc Ignition | HAI | UL746 | PLC 3 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| Hot-wire Ignition | HWI | UL746 | PLC 2 |
| Volume Resistivity | ASTMD257 | >2.5E+17 ohms·cm | |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 20 KV/mm |
| Dielectric Constant | 50Hz | ASTMD150 | 3.27 |
| 60Hz | ASTMD150 | 3.27 | |
| 1MHz | ASTMD150 | 3.10 |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | M级 | ASTMD785 | 92 |
| R级 | ASTMD785 | 127 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Gardner Impact | 23°C | ASTMD3029 | 149 J |
| Tensile Impact Strength | ASTMD1822 | 578 kJ/m² | |
| -30°C | ASTMD256 | 84 J/m | |
| 23°C | ASTMD256 | 370 J/m | |
| -30°C10 | ISO180/1A | 6.0 kJ/m² | |
| 23°C11 | ISO180/1A | 7.0 kJ/m² | |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 3200 J/m |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 74.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.