Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 4704 SABIC INNOVATIVE US
LEXAN™
Electrical applications、Lighting applications、Automotive Applications
Thermal stability、Middle flow
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 150 °C | |
| Specific Heat | ASTMC351 | 1260 J/kg/°C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 149 °C | |
| RTIElec | UL746 | 130 °C | |
| Flow:-40 to 95°C | ASTME831 | 8.1E-05 cm/cm/°C | |
| RTI | UL746 | 130 °C | |
| Thermal Conductivity | ASTMC177 | 0.21 W/m/K | |
| Flow:-40 to 40°C | ASTME831,ISO11359-2 | 6E-05 cm/cm/°C | |
| Evolution Calendar intelligent importer | UL746 | 130 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 127 |
| M级 | ASTMD785 | 92 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| Equilibrium,23°C,50%RH | ISO62 | 0.35 % | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.80到1.0 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 2.0 g/10min |
| Specific Volume | ASTMD792 | 0.835 cm³/g | |
| Saturation ,23℃ | ISO62 | 0.16 % | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 2.00 cm3/10min |
| ASTMD570 | 0.19 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| ASTMD638 | 2080 Mpa | ||
| Break | ASTMD638 | 77.9 Mpa | |
| fracture | ISO527-2/50 | 100 % | |
| Yield,50.0mm Span | ASTMD790 | 97.2 Mpa | |
| Break | ASTMD638 | 78 % | |
| yield | ISO527-2/50 | 7.0 % | |
| 50.0mm Span | ASTMD790 | 2330 Mpa | |
| Yield | ASTMD638 | 8.0 % | |
| fracture | ISO527-2/50 | 68.0 Mpa | |
| ISO178 | 66.0 Mpa | ||
| Yield | ASTMD638 | 65.5 Mpa | |
| yield | ISO527-2/50 | 68.0 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.600 | |
| Transmittance | 2540µm | ASTMD1003 | 85.0 % |
| Haze | 2540µm | ASTMD1003 | 1.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| ASTMD256 | 370 J/m | ||
| Gardner Impact | 23°C | ASTMD3029 | 149 J |
| Tensile Impact Strength | ASTMD1822 | 578 kJ/m² | |
| ISO180/1A | 7.0 kJ/m² | ||
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 74.0 J |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 3200 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| Flame Rating | 1.47mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/4704 |
|---|---|---|---|
| Dissipation Factor? | 50Hz | ASTMD150 | 1.6E-03 |
| 60Hz | ASTMD150 | 1.6E-03 | |
| 100Hz | ASTMD150 | 0.026 | |
| Hot-wire Ignition | HWI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 3 |
| Volume Resistivity | ASTMD257 | >2.5E+17 ohms·cm | |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 3 |
| Dielectric Constant | 60Hz | ASTMD150 | 3.27 |
| 50Hz | ASTMD150 | 3.27 | |
| Arc Resistance | ASTMD495 | PLC6 | |
| Dielectric Constant | 1MHz | ASTMD150 | 3.10 |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 20 KV/mm |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |