PC LEXAN™ HF1110 BK SABIC INNOVATIVE NANSHA
135
- Unit Price:$2805 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility｜High temperature resistan｜transparent
- Application Areas:High mobility｜High temperature resistan｜transparent
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 25 g/10 min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Moisture Absorption | 24 hr | ASTM D570 | 0.10 % |
| 平衡, 23°C | ASTM D570 | 0.35 % | |
| 平衡, 100°C | ASTM D570 | 0.58 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 126 °C |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Transmittance | 2540 µm | ASTM D1003 | 88.0 % |
| Haze | 2540 µm | ASTM D1003 | 1.0 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 断裂 | ASTM D638 | 65.0 Mpa | |
| Tensile Elongation | 断裂 | ASTM D638 | 120 % |
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 2300 Mpa |
| Flexural Strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 2 | |
| High Amp Arc Ignition | UL 746 | PLC 1 | |
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 | |
| Hot-wire Ignition | UL 746 | PLC 2 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 120 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 60 % | ||
| Rear Temperature | 250 到 270 °C | ||
| Middle Temperature | 260 到 280 °C | ||
| Front Temperature | 270 到 295 °C | ||
| Nozzle Temperature | 265 到 290 °C | ||
| Processing (Melt) Temp | 270 到 295 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.025 到 0.076 mm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 54.0 J |
| Tensile Impact Strength | ASTM D1822 | 378 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.