Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF1110 BK SABIC INNOVATIVE NANSHA
LEXAN™
High mobility、High temperature resistan、transparent
High mobility、High temperature resistan、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| RTI | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 126 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| Middle Temperature | 260 到 280 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 120 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 270 到 295 °C | ||
| Rear Temperature | 250 到 270 °C | ||
| Nozzle Temperature | 265 到 290 °C | ||
| Front Temperature | 270 到 295 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C | ASTM D570 | 0.35 % |
| 平衡, 100°C | ASTM D570 | 0.58 % | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 25 g/10 min |
| Moisture Absorption | 24 hr | ASTM D570 | 0.10 % |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| Flexural Strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| Tensile Strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 断裂 | ASTM D638 | 65.0 Mpa | |
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 2300 Mpa |
| Tensile Elongation | 断裂 | ASTM D638 | 120 % |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| Haze | 2540 µm | ASTM D1003 | 1.0 % |
| Transmittance | 2540 µm | ASTM D1003 | 88.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| Tensile Impact Strength | ASTM D1822 | 378 kJ/m² | |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 54.0 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HF1110 BK |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 2 | |
| Comparative Tracking Index | UL 746 | PLC 2 | |
| High Amp Arc Ignition | UL 746 | PLC 1 | |
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 |