PC SD POLYCA™ 301-4 SUMITOMO JAPAN
148
Unit Price:$3897 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2 kg | ISO 1133 | 4.0 g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 4.00 cm3/10min |
| Modeling Shrinkage | 流动 | 内部方法 | 0.50 到 0.70 % |
| 横向流动 | 内部方法 | 0.50 到 0.70 % | |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.20 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/Af | 130 °C |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Index of Refraction | ISO 489 | 1.585 | |
| Transmittance | 2000 µm | ISO 13468 | 89.0 % |
| Haze | 2000 µm | ISO 14782 | 0.40 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| 3.0 mm | UL 94 | HB | |
| 0.44 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-2 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | 2300 Mpa | |
| Tensile Stress | 屈服 | ISO 527-2 | 60.0 Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | 110 % |
| Flexural Modulus | ISO 178 | 2300 Mpa | |
| Flexural Stress | ISO 178 | 92.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume Resistivity | IEC 60093 | 3.0E+16 ohms·cm | |
| Dielectric Strength | 1.00 mm | IEC 60243-1 | 31 KV/mm |
| Relative Permittivity | 2.00 mm, 100 Hz | IEC 60250 | 3.00 |
| 2.00 mm, 1 MHz | IEC 60250 | 3.00 | |
| Dissipation Factor? | 2.00 mm, 100 Hz | IEC 60250 | 1.0E-3 |
| 2.00 mm, 1 MHz | IEC 60250 | 0.090 | |
| Comparative Tracking Index | IEC 60112 | 250 V |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 125 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Rear Temperature | 280 到 300 °C | ||
| Middle Temperature | 290 到 310 °C | ||
| Front Temperature | 310 到 330 °C | ||
| Nozzle Temperature | 310 到 330 °C | ||
| Mold Temperature | 70 到 100 °C | ||
| Screw Speed | 60 到 100 rpm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R 计秤 | ISO 2039-2 | 118 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179 | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.