PC 301-4 SUMITOMO JAPAN
SD POLYCA™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/Af | 130 °C |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| Hardness | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Rockwell Hardness | R 计秤 | ISO 2039-2 | 118 |
| Injection | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Middle Temperature | 290 到 310 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Rear Temperature | 280 到 300 °C | ||
| Nozzle Temperature | 310 到 330 °C | ||
| Drying Temperature | 125 °C | ||
| Front Temperature | 310 到 330 °C | ||
| Mold Temperature | 70 到 100 °C | ||
| Screw Speed | 60 到 100 rpm |
| Physical | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Modeling Shrinkage | 流动 | 内部方法 | 0.50 到 0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ISO 1133 | 4.0 g/10 min |
| Modeling Shrinkage | 横向流动 | 内部方法 | 0.50 到 0.70 % |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.20 % |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 4.00 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Tensile Strain | 断裂 | ISO 527-2 | 110 % |
| Tensile Modulus | ISO 527-2 | 2300 Mpa | |
| Flexural Modulus | ISO 178 | 2300 Mpa | |
| Tensile Stress | 屈服 | ISO 527-2 | 60.0 Mpa |
| Flexural Stress | ISO 178 | 92.0 Mpa |
| Optical | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Index of Refraction | ISO 489 | 1.585 | |
| Transmittance | 2000 µm | ISO 13468 | 89.0 % |
| Haze | 2000 µm | ISO 14782 | 0.40 % |
| Impact Properties | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179 | 无断裂 |
| Flammability | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-2 |
| 3.0 mm | UL 94 | HB | |
| 0.44 mm | UL 94 | V-2 | |
| 1.5 mm | UL 94 | HB |
| Electrical Properties | Test Condition | Test Method | SUMITOMO JAPAN/301-4 |
|---|---|---|---|
| Relative Permittivity | 2.00 mm, 1 MHz | IEC 60250 | 3.00 |
| Dielectric Strength | 1.00 mm | IEC 60243-1 | 31 KV/mm |
| Relative Permittivity | 2.00 mm, 100 Hz | IEC 60250 | 3.00 |
| Volume Resistivity | IEC 60093 | 3.0E+16 ohms·cm | |
| Dissipation Factor? | 2.00 mm, 1 MHz | IEC 60250 | 0.090 |
| Comparative Tracking Index | IEC 60112 | 250 V | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Dissipation Factor? | 2.00 mm, 100 Hz | IEC 60250 | 1.0E-3 |