PC LEXAN™ ML9330 BK1E519 SABIC INNOVATIVE US
111
Unit Price:$4431 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜Toughening｜UV resistance
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.00 cm3/10min |
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.40到0.80 % |
| TD:3.20mm | 内部方法 | 0.40到0.80 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| 平衡,23°C,50%RH | ISO62 | 0.15 % | |
| Outdoor Suitability | UL746C | f1 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear thermal expansion coefficient | MD:23到80°C | ISO11359-2 | 7.2E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C | |
| TD:23到80°C | ISO11359-2 | 7.7E-05 cm/cm/°C | |
| RTIElec | UL746 | 125 °C | |
| Evolution Calendar intelligent importer | UL746 | 115 °C | |
| RTI | UL746 | 120 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 134 °C |
| 0.45MPa,未退火,100mm跨距12 | ISO75-2/Be | 135 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 120 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 124 °C | |
| 1.8MPa,未退火,100mm跨距12 | ISO75-2/Ae | 124 °C | |
| Vicat Softening Temperature | -- | ASTMD152513,ISO306/B12013 | 142 °C |
| -- | ISO306/B50 | 140 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.8mm | UL94 | V-1 |
| 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| Oxygen Index | ISO4589-2 | 35 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Elongation | 断裂 | ISO527-2/50 | 130 % |
| Flexural Modulus | 50.0mm跨距5 | ASTMD790 | 2070 Mpa |
| --6 | ISO178 | 2200 Mpa | |
| Flexural Stress | --6,7 | ISO178 | 85.0 Mpa |
| 屈服,50.0mm跨距5 | ASTMD790 | 88.0 Mpa | |
| Tensile Modulus | --3 | ASTMD638 | 2100 Mpa |
| -- | ISO527-2/1 | 2100 Mpa | |
| Tensile Strength | 屈服4 | ASTMD638 | 58.0 Mpa |
| 屈服 | ISO527-2/50 | 55.0 Mpa | |
| 断裂4 | ASTMD638 | 61.0 Mpa | |
| 断裂 | ISO527-2/50 | 60.0 Mpa | |
| Tensile Elongation | 屈服4 | ASTMD638 | 6.0 % |
| 屈服 | ISO527-2/50 | 6.0 % | |
| 断裂4 | ASTMD638 | 130 % |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 17 KV/mm |
| 3.20mm,在油中 | IEC60243-1 | 16 KV/mm | |
| Dissipation Factor? | 50Hz | ASTMD150 | 2.4E-03 |
| 60Hz | ASTMD150 | 2.4E-03 | |
| 1MHz | ASTMD150,IEC60250 | 8.5E-03 | |
| 50Hz | IEC60250 | 1E-03 | |
| 60Hz | IEC60250 | 1E-03 | |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |
| IEC60112 | 225 V | ||
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Hot-wire Ignition | HWI | UL746 | PLC 1 |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 90.0 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 60 kJ/m² |
| 23°C | ISO179/1eA | 75 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 |
| 23°C | ISO179/1eU | 无断裂 | |
| Unnotched Izod Impact Strength | 23°C11 | 内部方法 | 1100 J/m |
| -30°C9 | ISO180/1U | 无断裂 | |
| 23°C9 | ISO180/1U | 无断裂 | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 52.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.