PC ML9330 BK1E519 SABIC INNOVATIVE US
LEXAN™
--
Flame retardant、Toughening、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML9330 BK1E519 |
|---|---|---|---|
| Vicat Softening Temperature | -- | ASTMD152513,ISO306/B12013 | 142 °C |
| RTIElec | UL746 | 125 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 120 °C |
| 1.8MPa,未退火,100mm跨距12 | ISO75-2/Ae | 124 °C | |
| Linear thermal expansion coefficient | TD:23到80°C | ISO11359-2 | 7.7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 124 °C |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B50 | 140 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 134 °C |
| RTI | UL746 | 120 °C | |
| Linear thermal expansion coefficient | MD:23到80°C | ISO11359-2 | 7.2E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 115 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,100mm跨距12 | ISO75-2/Be | 135 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/ML9330 BK1E519 |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 90.0 Mpa |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML9330 BK1E519 |
|---|---|---|---|
| Tensile Strength | 断裂 | ISO527-2/50 | 60.0 Mpa |
| Tensile Modulus | --3 | ASTMD638 | 2100 Mpa |
| Tensile Elongation | 断裂4 | ASTMD638 | 130 % |
| Tensile Strength | 断裂4 | ASTMD638 | 61.0 Mpa |
| Tensile Elongation | 断裂 | ISO527-2/50 | 130 % |
| Flexural Stress | 屈服,50.0mm跨距5 | ASTMD790 | 88.0 Mpa |
| --6,7 | ISO178 | 85.0 Mpa | |
| Flexural Modulus | 50.0mm跨距5 | ASTMD790 | 2070 Mpa |
| Tensile Strength | 屈服 | ISO527-2/50 | 55.0 Mpa |
| Tensile Modulus | -- | ISO527-2/1 | 2100 Mpa |
| Tensile Elongation | 屈服 | ISO527-2/50 | 6.0 % |
| 屈服4 | ASTMD638 | 6.0 % | |
| Tensile Strength | 屈服4 | ASTMD638 | 58.0 Mpa |
| Flexural Modulus | --6 | ISO178 | 2200 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/ML9330 BK1E519 |
|---|---|---|---|
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.40到0.80 % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.40到0.80 % |
| Outdoor Suitability | UL746C | f1 | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.00 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML9330 BK1E519 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 |
| Unnotched Izod Impact Strength | 23°C11 | 内部方法 | 1100 J/m |
| 23°C9 | ISO180/1U | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 60 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 52.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 75 kJ/m² |
| Unnotched Izod Impact Strength | -30°C9 | ISO180/1U | 无断裂 |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/ML9330 BK1E519 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| Flame Rating | 3.0mm | UL94 | 5VA |
| Oxygen Index | ISO4589-2 | 35 % | |
| Flame Rating | 0.8mm | UL94 | V-1 |
| 1.5mm | UL94 | V-0 | |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/ML9330 BK1E519 |
|---|---|---|---|
| Dissipation Factor? | 50Hz | ASTMD150 | 2.4E-03 |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dissipation Factor? | 60Hz | ASTMD150 | 2.4E-03 |
| Comparative Tracking Index | IEC60112 | 225 V | |
| Dissipation Factor? | 1MHz | ASTMD150,IEC60250 | 8.5E-03 |
| 60Hz | IEC60250 | 1E-03 | |
| 50Hz | IEC60250 | 1E-03 | |
| Hot-wire Ignition | HWI | UL746 | PLC 1 |
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 16 KV/mm |
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Dielectric Strength | 3.20mm,inOil | ASTMD149 | 17 KV/mm |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |