PC LEXAN™ HPX8R NA8A005T SABIC INNOVATIVE US
104
Unit Price:$4852 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 26MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility｜Easy to demould｜Biocompatibility
- Application Areas:Medical field｜medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 35 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 33.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| TD：3.20mm | 内部方法 | 0.40to0.80 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.12 % |
| 平衡,23°C,50%RH | ISO62 | 0.093 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 121 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 118 °C | |
| Vicat Softening Temperature | ASTMD152510 | 138 °C | |
| -- | ISO306/B50 | 138 °C | |
| -- | ISO306/B120 | 140 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 6.5E-05 cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 6.5E-05 cm/cm/°C | |
| TD：-40to95°C | ASTME831 | 7.4E-05 cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.4E-05 cm/cm/°C | |
| RTIElec | UL746 | 130 °C | |
| RTIStr | UL746 | 130 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 82.0 % |
| Haze | 2540µm | ASTMD1003 | 3.0 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | HB |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 0.8mm | IEC60695-2-13 | 825 °C |
| 3.0mm | IEC60695-2-13 | 850 °C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTMD638 | 2370 Mpa | |
| ISO527-2/1 | 2400 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 60.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 59.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 56.6 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.8 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 5.4 % |
| Tensile Elongation | 断裂 | ASTMD638 | 120 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 120 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2360 Mpa |
| ISO178 | 2250 Mpa | ||
| Flexural Strength | ISO178 | 92.9 Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 99.2 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | >1.0E+15 ohms | |
| Volume Resistivity | ASTMD257 | >1.0E+15 ohms·cm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | L计秤 | ASTMD785 | 90 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 30 kJ/m² |
| 23°C | ISO180/1A | 60 kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| 23°C | ISO180/1U | NoBreak | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 79.0 J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 30 kJ/m² |
| 23°C | ISO179/1eA | 60 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | ISO179/1eU | NoBreak |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.