Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HPX8R NA8A005T SABIC INNOVATIVE US
LEXAN™
Medical field、medical care
High mobility、Easy to demould、Biocompatibility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 118 °C |
| RTIElec | UL746 | 130 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 138 °C |
| Linear thermal expansion coefficient | TD：-40to95°C | ASTME831 | 7.4E-05 cm/cm/°C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 121 °C |
| RTIStr | UL746 | 130 °C | |
| Vicat Softening Temperature | ASTMD152510 | 138 °C | |
| -- | ISO306/B120 | 140 °C | |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 6.5E-05 cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 6.5E-05 cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.4E-05 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Rockwell Hardness | L计秤 | ASTMD785 | 90 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.093 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 35 g/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.40to0.80 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 33.0 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.12 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2360 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 56.6 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 120 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 120 % |
| Tensile Modulus | ISO527-2/1 | 2400 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 60.0 Mpa |
| Flexural Modulus | ISO178 | 2250 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 99.2 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.8 % |
| Tensile Stress | 屈服 | ISO527-2/50 | 59.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 5.4 % |
| Flexural Strength | ISO178 | 92.9 Mpa | |
| Tensile Modulus | ASTMD638 | 2370 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 82.0 % |
| Haze | 2540µm | ASTMD1003 | 3.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 30 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 30 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 79.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 60 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 60 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 850 °C |
| Flame Rating | 1.5mm | UL94 | HB |
| Glow Wire Ignition Temperature | 0.8mm | IEC60695-2-13 | 825 °C |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX8R NA8A005T |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | >1.0E+15 ohms | |
| Volume Resistivity | ASTMD257 | >1.0E+15 ohms·cm |