PC LNP™ LUBRILOY™ D20001 BK1E055 SABIC INNOVATIVE US
111
Unit Price:$4592 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant
- Application Areas:Electrical appliances｜Plastic bag｜Aerospace Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Volume flow Rate | 300°C/1.2 kg | ASTM D1238 | 15.7 cm3/10min |
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 0.50 % |
| 横向流动 : 24小时 | ASTM D955 | 0.60 % | |
| 横向流量 : 24小时 | ISO 294-4 | 0.57 % | |
| 流量 : 24小时 | ISO 294-4 | 0.53 % | |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 97.0 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 89.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4 | ISO 75-2/Af | 94.0 °C | |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 6.6E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 6.7E-5 cm/cm/°C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm, Testing by SABIC | UL 94 | V-0 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2550 Mpa |
| -- | ISO 527-2/1 | 2600 Mpa | |
| Tensile Strength | 屈服 | ASTM D638 | 67.0 Mpa |
| 屈服 | ISO 527-2 | 62.0 Mpa | |
| 断裂 | ASTM D638 | 60.0 Mpa | |
| 断裂 | ISO 527-2 | 54.0 Mpa | |
| Tensile Elongation | 屈服 | ASTM D638 | 4.5 % |
| 屈服 | ISO 527-2 | 4.3 % | |
| 断裂 | ASTM D638 | 6.5 % | |
| 断裂 | ISO 527-2 | 6.7 % | |
| Flexural Modulus | -- | ASTM D790 | 2820 Mpa |
| -- | ISO 178 | 2800 Mpa | |
| Flexural Strength | -- | ASTM D790 | 103 Mpa |
| -- | ISO 178 | 102 Mpa | |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.090 |
| Static | ASTM D3702 | 0.22 | |
| Specific Wear Rate | ASTM D3702 | 6.0E+6 10^-8 mm³/N·m |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 80 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Rear Temperature | 250 到 260 °C | ||
| Middle Temperature | 255 到 265 °C | ||
| Front Temperature | 260 到 270 °C | ||
| Processing (Melt) Temp | 255 到 290 °C | ||
| Mold Temperature | 40 到 65 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Screw Speed | 30 到 60 rpm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1600 J/m |
| 23°C 4 | ISO 180/1U | 100 kJ/m² | |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 51.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.