Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC D20001 BK1E055 SABIC INNOVATIVE US
LNP™ LUBRILOY™
Electrical appliances、Plastic bag、Aerospace Applications
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D20001 BK1E055 |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 6.6E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4 | ISO 75-2/Af | 94.0 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 6.7E-5 cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 89.0 °C |
| 0.45 MPa, 未退火, 3.20 mm | 97.0 °C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/D20001 BK1E055 |
|---|---|---|---|
| Suggested Max Moisture | 0.020 % | ||
| Middle Temperature | 255 到 265 °C | ||
| Processing (Melt) Temp | 255 到 290 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Rear Temperature | 250 到 260 °C | ||
| Drying Temperature | 80 °C | ||
| Front Temperature | 260 到 270 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Mold Temperature | 40 到 65 °C | ||
| Screw Speed | 30 到 60 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/D20001 BK1E055 |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 0.50 % |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| Modeling Shrinkage | 横向流动 : 24小时 | ASTM D955 | 0.60 % |
| 横向流量 : 24小时 | ISO 294-4 | 0.57 % | |
| Melt Volume flow Rate | 300°C/1.2 kg | ASTM D1238 | 15.7 cm3/10min |
| Modeling Shrinkage | 流量 : 24小时 | ISO 294-4 | 0.53 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D20001 BK1E055 |
|---|---|---|---|
| Tensile Elongation | 屈服 | ISO 527-2 | 4.3 % |
| Tensile Modulus | -- | ISO 527-2/1 | 2600 Mpa |
| Flexural Strength | ISO 178 | 102 Mpa | |
| Specific Wear Rate | ASTM D3702 | 6.0E+6 10^-8 mm³/N·m | |
| Flexural Strength | -- | ASTM D790 | 103 Mpa |
| Flexural Modulus | ISO 178 | 2800 Mpa | |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.090 |
| Tensile Strength | 断裂 | ISO 527-2 | 54.0 Mpa |
| ASTM D638 | 60.0 Mpa | ||
| Tensile Elongation | 6.5 % | ||
| Tensile Modulus | -- 2 | 2550 Mpa | |
| Flexural Modulus | -- | ASTM D790 | 2820 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2 | 6.7 % |
| Tensile Strength | 屈服 | ASTM D638 | 67.0 Mpa |
| ISO 527-2 | 62.0 Mpa | ||
| Tensile Elongation | ASTM D638 | 4.5 % | |
| Coefficient of Friction | Static | ASTM D3702 | 0.22 |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/D20001 BK1E055 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1600 J/m |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 51.0 J |
| Unnotched Izod Impact Strength | 23°C 4 | ISO 180/1U | 100 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/D20001 BK1E055 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm, Testing by SABIC | UL 94 | V-0 |