PC PANLITE® MN-3600H TEIJIN JAPAN
258
Unit Price:$2772 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:heat-resisting｜Flame retardant｜Good impact resistance｜Good liquidity｜Halogen-free
- Application Areas:Electrical field｜Electronic field｜Automotive sector
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Volume flow Rate | 280°C/2.16kg | ISO1133 | 17.5 cm3/10min |
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 % |
| MD:4.00mm | 内部方法 | 0.50to0.70 % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.22 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ASTM D648/ISO 75 | 125 ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000070 mm/mm.℃ | |
| RTIStr | 1.5mm | UL746 | 95.0 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 125 °C |
| 1.8MPa,未退火 | ISO75-2/A | 112 °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| TD | ISO11359-2 | 7E-05 cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 95.0 °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 95.0 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 930 °C |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 875 °C |
| 1.5mm | IEC60695-2-13 | 825 °C | |
| 2.0mm | IEC60695-2-13 | 825 °C | |
| 3.0mm | IEC60695-2-13 | 825 °C | |
| Flame Rating | 0.45mm | UL94 | HB |
| 1.0mm | UL94 | V-1 | |
| 1.5mm | UL94 | V-0 | |
| 2.0mm | UL94 | 5VB | |
| 3.0mm | UL94 | 5VA | |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| 1.5mm | IEC60695-2-12 | 930 °C | |
| 2.0mm | IEC60695-2-12 | 960 °C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTM D638/ISO 527 | 2350 kg/cm²(MPa)[Lb/in²] | |
| Tensile Strength | ASTM D638/ISO 527 | 60.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | 7.0 % | |
| Flexural Modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 95.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 100 % | |
| Flexural Modulus | ISO178 | 2300 Mpa | |
| Flexural Stress | ISO178 | 95.0 Mpa | |
| Tensile Modulus | ISO527-2/1 | 2350 Mpa | |
| Tensile Stress | 屈服 | ISO527-2/50 | 60.0 Mpa |
| 断裂 | ISO527-2/50 | 50.0 Mpa | |
| Tensile Strain | 屈服 | ISO527-2/50 | 7.0 % |
| 断裂 | ISO527-2/50 | 100 % |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | NoBreak |
| Other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Remarks | 以上加工数据，为参考值.以生产厂商设备的实际状况而进行调整 | ||
| characteristic | 抗撞击性良好、耐热性高、良好的流动性、无卤、阻燃性能 | ||
| Color | 不透明 | ||
| purpose | 电气/电子应用领域、汽车领域的应用 |
| Physical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Modeling Shrinkage | ASTM D955 | 0.50-0.70 % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.22 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.