Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC MN-3600H TEIJIN JAPAN
PANLITE®
Electrical field、Electronic field、Automotive sector
heat-resisting、Flame retardant、Good impact resistance、Good liquidity、Halogen-free
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 95.0 °C |
| RTIElec | 95.0 °C | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 125 °C |
| RTIStr | 1.5mm | UL746 | 95.0 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 112 °C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 cm/cm/°C |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.000070 mm/mm.℃ | |
| Heat Deflection Temperature | ASTM D648/ISO 75 | 125 ℃（℉） |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Flexural Strength | ASTM D790/ISO 178 | 95.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 100 % | |
| Tensile Stress | 断裂 | ISO527-2/50 | 50.0 Mpa |
| Tensile Strength | ASTM D638/ISO 527 | 60.0 kg/cm²(MPa)[Lb/in²] | |
| Tensile Strain | 断裂 | ISO527-2/50 | 100 % |
| Tensile Modulus | ISO527-2/1 | 2350 Mpa | |
| ASTM D638/ISO 527 | 2350 kg/cm²(MPa)[Lb/in²] | ||
| Tensile Elongation | 7.0 % | ||
| Flexural Modulus | ISO178 | 2300 Mpa | |
| Tensile Stress | 屈服 | ISO527-2/50 | 60.0 Mpa |
| Tensile Strain | 7.0 % | ||
| Flexural Stress | ISO178 | 95.0 Mpa | |
| Flexural Modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Melt Volume flow Rate | 280°C/2.16kg | ISO1133 | 17.5 cm3/10min |
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 % |
| MD:4.00mm | 0.50to0.70 % | ||
| Moisture Absorption | 23°C,24hr | ISO62 | 0.22 % |
| Other | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Color | 不透明 | ||
| purpose | 电气/电子应用领域、汽车领域的应用 | ||
| Remarks | 以上加工数据，为参考值.以生产厂商设备的实际状况而进行调整 | ||
| characteristic | 抗撞击性良好、耐热性高、良好的流动性、无卤、阻燃性能 |
| Physical Properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.22 % | |
| Modeling Shrinkage | ASTM D955 | 0.50-0.70 % |
| Impact Properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | NoBreak |
| Flammability | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 825 °C |
| Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 930 °C |
| 3.0mm | 930 °C | ||
| 1.0mm | 960 °C | ||
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 825 °C |
| Flame Rating | 2.0mm | UL94 | 5VB |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 875 °C |
| 2.0mm | 825 °C | ||
| Flame Rating | 3.0mm | UL94 | 5VA |
| 1.5mm | V-0 | ||
| Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 960 °C |
| Flame Rating | 1.0mm | UL94 | V-1 |
| 0.45mm | HB |
| Electrical Properties | Test Condition | Test Method | TEIJIN JAPAN/MN-3600H |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms |