PC LEXAN™ 505R SABIC INNOVATIVE US
118
Unit Price:$3261 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:Middle flow｜Thermal stability
- Application Areas:Lighting applications｜Plastic bag
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density / Specific Gravity | ASTMD792 | 1.26 g/cm³ | |
| ISO1183 | 1.25 g/cm³ | ||
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 7.0 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 7.00 cm3/10min |
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.20to0.60 % |
| MD：3.20mm | 内部方法 | 0.50to0.70 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.31 % |
| 平衡,23°C,50%RH | ISO62 | 0.13 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat Softening Temperature | -- | ISO306/B50 | 141 °C |
| -- | ISO306/B120 | 143 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 4.7E-05 cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 4E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| Thermal Conductivity | ISO8302 | 0.21 W/m/K | |
| RTIElec | UL746 | 130 °C | |
| Evolution Calendar intelligent importer | UL746 | 130 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 143 °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 144 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 138 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 136 °C | |
| 1.8MPa,Annealed | ISO75-2/Ae | 136 °C | |
| Vicat Softening Temperature | ASTMD152514 | 149 °C | |
| RTIStr | UL746 | 130 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | V-0 |
| 3.0mm | UL94 | 5VA | |
| Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 825 °C |
| Oxygen Index | ISO4589-2 | 37 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTMD638 | 3930 Mpa | |
| ISO527-2/1 | 3300 Mpa | ||
| Flexural Strength | ISO178 | 95.0 Mpa | |
| Break,50.0mmSpan | ASTMD790 | 108 Mpa | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 11.0 mg |
| Tensile Strength | 屈服 | ASTMD638 | 63.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/5 | 60.0 Mpa |
| Tensile Strength | Break | ASTMD638 | 48.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 45.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 3.0 % |
| Tensile Strain | 屈服 | ISO527-2/5 | 5.0 % |
| Tensile Elongation | 断裂 | ASTMD638 | 12 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 7.0 % |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 3530 Mpa |
| ISO178 | 3400 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor? | 60Hz | IEC60250 | 1E-03 |
| 1MHz | IEC60250 | 0.010 | |
| Comparative Tracking Index | IEC60112 | 150 V | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 33 KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 KV/mm | |
| 3.20mm,在油中 | IEC60243-1 | 16 KV/mm | |
| Relative Permittivity | 50Hz | IEC60250 | 2.90 |
| 60Hz | IEC60250 | 2.90 | |
| 1MHz | IEC60250 | 2.80 | |
| Dissipation Factor? | 50Hz | IEC60250 | 1E-03 |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 115 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C8 | ISO179/1eU | NoBreak |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 80 J/m |
| 23°C | ASTMD256 | 110 J/m | |
| -30°C10 | ISO180/1A | 8.0 kJ/m² | |
| -30°C11 | ISO180/1A | 8.0 kJ/m² | |
| 23°C11 | ISO180/1A | 10 kJ/m² | |
| 23°C10 | ISO180/1A | 8.0 kJ/m² | |
| 23°C | ASTMD4812 | 1600 J/m | |
| Notched Izod impact strength | -30°C10 | ISO180/1U | NoBreak |
| -30°C11 | ISO180/1U | 130 kJ/m² | |
| Charpy Notched Impact Strength | -30°C8 | ISO179/1eA | 9.0 kJ/m² |
| 23°C9 | ISO179/1eA | 9.0 kJ/m² | |
| 23°C8 | ISO179/1eA | 10 kJ/m² | |
| 23°C | ISO179/2C | 15 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C9 | ISO179/1eU | NoBreak |
| -30°C8 | ISO179/1eU | NoBreak | |
| 23°C9 | ISO179/1eU | NoBreak | |
| Notched Izod impact strength | 23°C11 | ISO180/1U | NoBreak |
| 23°C10 | ISO180/1U | NoBreak | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 61.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.