POM TENAC™-C HC460 ASAHI JAPAN
207
- Unit Price:$3529 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:UV resistance｜scratch resistance ｜wear resistant｜Medium viscosity
- Application Areas:Engineering accessories｜Shell｜Automotive sector｜Engine parts｜Application in the automo｜currency
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 8.0 g/10min |
| Modeling Shrinkage | MD | 内部方法 | 1.6到2.0 % |
| Moisture Absorption | 23°C,24hr,50%RH | ASTMD570 | 0.20 % |
| Melt index | ISO 1133 | 8.0 g/10 min | |
| Modeling Shrinkage | MD | Internal Method | 1.6-2.0 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTMD648 | 163 °C |
| 0.45MPa,未退火 | ISO75-2/B | 158 °C | |
| 1.8MPa,未退火 | ASTMD648 | 124 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 102 °C | |
| Linear thermal expansion coefficient | MD | ASTMD696,ISO11359-2 | 1E-04 cm/cm/°C |
| Specific Heat | 1470 J/kg/°C | ||
| Thermal Conductivity | 0.23 W/m/K | ||
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 158 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 102 °C | |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| Burning Rate | UL94 | HB |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | HB |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ISO527-2 | 2750 Mpa | |
| Tensile Stress | 屈服 | ISO527-2 | 66.0 Mpa |
| -- | ASTMD638 | 64.0 Mpa | |
| Tensile Elongation | 断裂 | ASTMD638,ISO527-2 | 40 % |
| Flexural Modulus | ASTMD790,ISO178 | 2600 Mpa | |
| Flexural Strength | ASTMD790 | 88.0 Mpa | |
| Tensile Modulus | 23℃ | ISO 527-2 | 3000 Mpa |
| Tensile Stress | 屈服, 23℃ | ISO 527-2 | 69.0 Mpa |
| Tensile Strain | 断裂,23℃ | ISO 527-2 | 55 % |
| Charpy Notched Impact Strength | ISO 179 | 7.0 kJ/m² | |
| Tensile Modulus | ASTM D638/ISO 527 | 3000(MPa) kg/cm²(MPa)[Lb/in²] |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 117 |
| M级 | ASTMD785 | 88 |
| Other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 耐磨蚀性良好 |
| Physical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.41 | |
| Modeling Shrinkage | ASTM D955 | 1.6-2.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.