POM HC460 ASAHI JAPAN
TENAC™-C
Engineering accessories、Shell、Automotive sector、Engine parts、Application in the automo、currency
UV resistance、scratch resistance 、wear resistant、Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| Heat Deflection Temperature | 1.8MPa,未退火 | ASTMD648 | 124 °C |
| Linear thermal expansion coefficient | MD | ASTMD696,ISO11359-2 | 1E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 158 °C |
| 0.45MPa,未退火 | ISO75-2/B | 158 °C | |
| Specific Heat | 1470 J/kg/°C | ||
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 102 °C |
| Burning Rate | UL94 | HB | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 102 °C |
| Thermal Conductivity | 0.23 W/m/K | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTMD648 | 163 °C |
| Hardness | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 117 |
| M级 | ASTMD785 | 88 |
| Mechanical Properties | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Tensile Strain | 断裂,23℃ | ISO 527-2 | 55 % |
| Flexural Modulus | ASTMD790,ISO178 | 2600 Mpa | |
| Tensile Modulus | 23℃ | ISO 527-2 | 3000 Mpa |
| Flexural Strength | ASTMD790 | 88.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 7.0 kJ/m² | |
| Tensile Stress | 屈服 | ISO527-2 | 66.0 Mpa |
| -- | ASTMD638 | 64.0 Mpa | |
| 屈服, 23℃ | ISO 527-2 | 69.0 Mpa | |
| Tensile Modulus | ISO527-2 | 2750 Mpa | |
| ASTM D638/ISO 527 | 3000(MPa) kg/cm²(MPa)[Lb/in²] | ||
| Tensile Elongation | 断裂 | ASTMD638,ISO527-2 | 40 % |
| Physical | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Modeling Shrinkage | MD | 内部方法 | 1.6到2.0 % |
| Moisture Absorption | 23°C,24hr,50%RH | ASTMD570 | 0.20 % |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 8.0 g/10min |
| Modeling Shrinkage | MD | Internal Method | 1.6-2.0 % |
| Melt index | ISO 1133 | 8.0 g/10 min |
| Other | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| characteristic | 耐磨蚀性良好 |
| Physical Properties | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.41 | |
| Modeling Shrinkage | ASTM D955 | 1.6-2.0 % |
| Flammability | Test Condition | Test Method | ASAHI JAPAN/HC460 |
|---|---|---|---|
| Flame Rating | 0.75mm | UL94 | HB |