POM Delrin® 127UV DUPONT USA
160
Unit Price:$7776 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 73MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Flame retardant enhance
- Application Areas:Medical supplies
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.42 | g/cm³ | |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 2.4 | g/10min |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 1.90 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.9 | % |
| MD | ISO294-4 | 2.1 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 | % |
| Saturation,23°C,2.00mm | ISO62 | 1.2 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.30 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 3000 | Mpa | |
| tensile strength | Yield | ISO527-2 | 70.0 | Mpa |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 13 | kJ/m² |
| Rockwell hardness | M-Sale | ISO2039-2 | 92 | |
| R-Sale | ISO2039-2 | 120 | ||
| elongation | Yield | ISO527-2 | 23 | % |
| Nominal tensile fracture strain | ISO527-2 | 45 | % | |
| Bending modulus | ISO178 | 2700 | Mpa | |
| bending strength | 3.5%Strain | ISO178 | 80.5 | Mpa |
| -- | ISO178 | 72.0 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 11 | kJ/m² |
| 23°C | ISO179/1eA | 15 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 350 | kJ/m² |
| 23°C | ISO179/1eU | 400 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 11 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 93.0 | °C | |
| vicat softening point | ISO306/B50 | 160 | °C | |
| Melting temperature | ISO11357-3 | 178 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+13 | ohms·cm | |
| Relative permittivity | 100Hz | IEC60250 | 3.50 | |
| 1MHz | IEC60250 | 3.40 | ||
| Leakage Trace Index | IEC60112 | 600 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00mm | ISO3795 | 28 | mm/min |
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 1.5E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 16.0 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.