density

ISO1183

g/cm³

1

Melt Volume-Flow Rate (MVR)

190°C/2.16kg

ISO1133

cm3/10min

1

Melt mass flow rate

190°C/2.16kg

ISO1133

g/10min

2

Shrinkage rate

TD

ISO294-4

%

1

Shrinkage rate

MD

ISO294-4

%

2

Water absorption rate

23°C,24hr

ISO62

%

0

Water absorption rate

饱和,23°C,2.00mm

ISO62

%

1

Water absorption rate

平衡,23°C,2.00mm,50%RH

ISO62

%

0

Nominal tensile fracture strain

ISO527-2

%

4

Charpy Notched Impact Strength

-30°C

ISO179/1eA

kJ/m²

1

Charpy Notched Impact Strength

23°C

ISO179/1eA

kJ/m²

1

Impact strength of simply supported beam without notch

-30°C

ISO179/1eU

kJ/m²

3

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

4

Tensile modulus

ISO527-2

Mpa

3

tensile strength

屈服

ISO527-2

Mpa

7

elongation

屈服

ISO527-2

%

2

Bending modulus

ISO178

Mpa

2

bending strength

3.5%Strain

ISO178

Mpa

8

bending strength

--

ISO178

Mpa

7

Impact strength of cantilever beam gap

-40°C

ISO180/1A

kJ/m²

1

Impact strength of cantilever beam gap

23°C

ISO180/1A

kJ/m²

1

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

9

Melting temperature

ISO11357-3

°C

1

vicat softening point

ISO306/B50

°C

1

Linear coefficient of thermal expansion

MD

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD

ISO11359-2

cm/cm/°C

1

Leakage Trace Index

IEC60112

V

6

Volume resistivity

IEC60093

ohms·cm

1

Fogging-G-value

condensate

ISO6452

g

1

Burning rate

1.00mm

ISO3795

mm/min

2

Emission

VDA275

mg/kg

<

EmissionofOrganicCompounds

VDA277

µgC/g

1