PA66 Amilan® CM3004G-30 RD TORAY JAPAN
147
Unit Price:$3082 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜ Glass fiber reinforced b｜Filler: Glass fiber reinf｜Flame retardant grade｜30% filler by weight｜halogen-containing
- Application Areas:Office supplies｜Automotive sector｜building materials｜Electronic field｜Electrical field
- Color:--
- Grade:Halogen-free flame retardant grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Moisture Absorption | 23℃，24小时 | ASTM D-570 | 无水｜0.4 % |
| 23℃，24小时 | ASTM D-570 | 1.3%水｜- % | |
| Density / Specific Gravity | ASTM D-792 | 无水｜1.59 | |
| ASTM D-792 | 1.3%水｜- | ||
| 23°C | g/cm³ | 1.59 -- | |
| Modeling Shrinkage | TD:3.00mm3 | % | 0.60到0.90 -- |
| MD:3.00mm4 | % | 0.20到0.50 -- | |
| Moisture Absorption | 23°C,24hr | % | 0.60 -- |
| 饱和,23°C | % | 4.0 -- |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion | ASTM D-696 | 无水｜2 10-5cm/cm.℃ | |
| ASTM D-696 | 1.3%水｜- | ||
| Deflection Temperature Under Load? | 18.6kg/cm2 | ASTM D-648 | 无水｜251 °C |
| 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- °C | |
| Melting Temperature | 差示扫描测热计DSC法 | 265 °C | |
| Flame Rating | UL 94 | 无水｜V-0 | |
| UL 94 | 1.3%水｜- | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | °C | 251 -- |
| Melting temperature | °C | 265 -- | |
| Linear thermal expansion coefficient | MD | cm/cm/°C | 2E-05 -- |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.40mm | V-0 -- |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume Resistivity | ASTM D-257 | 1.3%水｜8×1013 Ω.cm | |
| Dielectric Strength | 1/8" | ASTM D-149 | 无水｜38 KV/mm |
| 1/8" | ASTM D-149 | 1.3%水｜33 KV/mm | |
| Comparative Tracking Index | UL 746 | 无水｜200 V | |
| UL 746 | 1.3%水｜- V | ||
| Loss factor | 106Hz | ASTM D-150 | 无水｜0.003-0.009 |
| 106Hz | ASTM D-150 | 1.3%水｜- | |
| Arc Resistance | 1/8" | ASTM D-495 | 无水｜70-80 S |
| 1/8" | ASTM D-495 | 1.3%水｜- S | |
| Volume Resistivity | ASTM D-257 | 无水｜8×1014 Ω.cm | |
| ohms·cm | 1E+15 1E+13 | ||
| Dielectric Strength | kV/mm | 38 33 | |
| Dielectric Constant | 23°C,1kHz | 4.00 -- | |
| 23°C,1MHz | 0.0100 -- | ||
| Arc Resistance | sec | 70.0 -- | |
| Comparative Tracking Index | CTI | V | 200 -- |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Izod Impact Strength | 23℃，无缺口1/8 | 无水｜65 kg.cm/cm | |
| 23℃，无缺口1/8 | 1.3%水｜70 kg.cm/cm | ||
| Tensile Strength (Break) | 23℃ | ASTM D-638 | 无水｜1640 kg/cm2 |
| 23℃ | ASTM D-638 | 1.3%水｜1350 kg/cm2 | |
| Tensile Elongation?(Break) | 23℃ | ASTM D-638 | 无水｜5 % |
| 23℃ | ASTM D-638 | 1.3%水｜5 % | |
| Flexural strength | 23℃ | ASTM D-790 | 无水｜2490 kg/cm2 |
| 23℃ | ASTM D-790 | 1.3%水｜2000 kg/cm2 | |
| Flexural Modulus | 23℃ | ASTM D-790 | 无水｜93200 kg/cm2 |
| 23℃ | ASTM D-790 | 1.3%水｜65000 kg/cm2 | |
| Tensile Strain | 断裂,-40°C | % | 2.5 -- |
| 断裂,23°C | % | 3.0 3.0 | |
| 断裂,80°C | % | 4.5 -- | |
| Flexural Modulus | -40°C | MPa | 10200 -- |
| 23°C | MPa | 9300 6500 | |
| 80°C | MPa | 5500 -- | |
| Flexural Stress | -40°C | MPa | 275 -- |
| 23°C | MPa | 250 | |
| 80°C | MPa | 150 -- | |
| Taber Abrasion Resistance | 1000Cycles | mg | 26.0 -- |
| Tensile Stress | -40°C | MPa | 190 -- |
| 23°C | MPa | 165 | |
| 80°C | MPa | 110 -- |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R计秤,23°C | 121 -- |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 -- |
| 23°C | kJ/m² | 9.5 14 | |
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 65 70 |
| Other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Reinforcement Content | 无水｜30 wt% | ||
| 1.3%水｜- wt% |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.