Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3004G-30 RD TORAY JAPAN
Amilan®
Office supplies、Automotive sector、building materials、Electronic field、Electrical field
Flame retardant、Glass fiber reinforced、 Glass fiber reinforced b、Filler: Glass fiber reinf、Flame retardant grade、30% filler by weight、halogen-containing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Flame Rating | UL 94 | 1.3%水｜- | |
| Melting Temperature | 差示扫描测热计DSC法 | 265 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | °C | 251 -- |
| Coefficient of Linear Thermal Expansion | ASTM D-696 | 1.3%水｜- | |
| Deflection Temperature Under Load? | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- °C |
| Linear thermal expansion coefficient | MD | cm/cm/°C | 2E-05 -- |
| Coefficient of Linear Thermal Expansion | ASTM D-696 | 无水｜2 10-5cm/cm.℃ | |
| Melting temperature | °C | 265 -- |
| Hardness | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Rockwell Hardness | R计秤,23°C | 121 -- |
| Physical | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Density / Specific Gravity | ASTM D-792 | 1.3%水｜- | |
| Modeling Shrinkage | MD:3.00mm4 | % | 0.20到0.50 -- |
| TD:3.00mm3 | 0.60到0.90 -- | ||
| Moisture Absorption | 23°C,24hr | 0.60 -- | |
| 饱和,23°C | 4.0 -- | ||
| 23℃，24小时 | ASTM D-570 | 1.3%水｜- % | |
| Density / Specific Gravity | 23°C | g/cm³ | 1.59 -- |
| Mechanical Properties | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Flexural Stress | -40°C | MPa | 275 -- |
| Flexural Modulus | 23℃ | ASTM D-790 | 1.3%水｜65000 kg/cm2 |
| -40°C | MPa | 10200 -- | |
| Tensile Strain | 断裂,80°C | % | 4.5 -- |
| Tensile Strength (Break) | 23℃ | ASTM D-638 | 1.3%水｜1350 kg/cm2 |
| Tensile Stress | -40°C | MPa | 190 -- |
| Tensile Strain | 断裂,23°C | % | 3.0 3.0 |
| Flexural Modulus | 80°C | MPa | 5500 -- |
| 23°C | 9300 6500 | ||
| Izod Impact Strength | 23℃，无缺口1/8 | 1.3%水｜70 kg.cm/cm | |
| Flexural Stress | 80°C | MPa | 150 -- |
| Taber Abrasion Resistance | 1000Cycles | mg | 26.0 -- |
| Tensile Stress | 23°C | MPa | 165 |
| Tensile Strain | 断裂,-40°C | % | 2.5 -- |
| Flexural Stress | 23°C | MPa | 250 |
| Tensile Elongation?(Break) | 23℃ | ASTM D-638 | 1.3%水｜5 % |
| Flexural strength | ASTM D-790 | 1.3%水｜2000 kg/cm2 | |
| Tensile Stress | 80°C | MPa | 110 -- |
| Other | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Reinforcement Content | 1.3%水｜- wt% |
| Impact Properties | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 65 70 |
| Charpy Notched Impact Strength | 9.5 14 | ||
| -40°C | 7.0 -- |
| Flammability | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Flame Rating | 0.40mm | V-0 -- |
| Electrical Properties | Test Condition | Test Method | TORAY JAPAN/CM3004G-30 RD |
|---|---|---|---|
| Dielectric Constant | 23°C,1MHz | 0.0100 -- | |
| Dielectric Strength | 1/8" | ASTM D-149 | 1.3%水｜33 KV/mm |
| kV/mm | 38 33 | ||
| Comparative Tracking Index | CTI | V | 200 -- |
| Volume Resistivity | ohms·cm | 1E+15 1E+13 | |
| Comparative Tracking Index | UL 746 | 1.3%水｜- V | |
| Loss factor | 106Hz | ASTM D-150 | 1.3%水｜- |
| Volume Resistivity | ASTM D-257 | 无水｜8×1014 Ω.cm | |
| Arc Resistance | 1/8" | ASTM D-495 | 1.3%水｜- S |
| Dielectric Constant | 23°C,1kHz | 4.00 -- | |
| Arc Resistance | sec | 70.0 -- |