PA66

PA66 Zytel® 80G33L DUPONT CANADA

243

Unit Price:US$ 4,331 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
36MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PA66 Zytel® 80G33L DUPONT USA

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability
Application Areas:Automotive interior parts｜Electrical applications
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

Filling analysis	Test Method	Test Result
Melt density		1.12 g/cm³
Top out temperature		210 °C
Specific Heat Capacity of Melt		2200 J/kg/°C
Thermal Conductivity of Melt		0.22 W/m/K
Emission of Organic Compounds	VDA 277	25.0 µgC/g
Odor	VDA 270	3.00

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	91 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	74 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	80 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS combustion rate		FMVSS 302	SE/B
Extreme Oxygen Index		ISO 4589-2	23 %
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Burning rate	1.00 mm	ISO 3795	23 mm/min
雾化 - G-value (condensate)		ISO 6452	8.0E-4 g

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	7400 Mpa
Tensile strain	Break	ISO 527-2	4.0 %
tensile strength	Break	ISO 527-2	142 Mpa
Tensile modulus		ISO 527-2	8700 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			285 to 305 °C
Melt Temperature, Optimum			295 °C
Mold temperature			50 to 100 °C
Mold Temperature, Optimum			80 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.2E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	247 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262 °C
Effective thermal diffusivity coefficient			8.50E-8 m²/s

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.5 %
	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	4.5 %
	Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.83 %
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.80 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 80G33L DUPONT CANADA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet