PA66 Zytel® 70G33HS1L-BK DUPONT USA
123
Unit Price:$3126 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:Thermal stability｜high strength｜Glass fiber reinforced
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 1.1 % |
| 流量 | ISO 294-4 | 0.30 % | |
| Moisture Absorption | 饱和, 23°C, 2.00 mm | ISO 62 | 5.7 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.8 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 261 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 252 °C | |
| Melting Temperature | ISO 11357-3 | 262 °C | |
| Linear thermal expansion coefficient | 流动 | ISO 11359-2 | 1.8E-5 cm/cm/°C |
| 流动 : -40 到 23°C | ISO 11359-2 | 2.4E-5 cm/cm/°C | |
| 流动 : 55 到 160°C | ISO 11359-2 | 1.3E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 8.3E-5 cm/cm/°C | |
| 横向 : -40 到 23°C | ISO 11359-2 | 6.5E-5 cm/cm/°C | |
| 横向 : 55 到 160°C | ISO 11359-2 | 1.4E-4 cm/cm/°C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning Rate | 1.00 mm | ISO 3795 | 28 mm/min |
| UL flame retardant rating | 0.75 mm | UL 94, IEC 60695-11-10, -20 | HB |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| FMVSS Flammability | FMVSS 302 | B | |
| Haze | ISO 6452 | 6.0E-4 g |
| Fill Analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 210 °C | ||
| Emission of Organic Compounds | VDA 277 | 10.0 µgC/g | |
| Odor | VDA 270 | 3.00 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | 11000 Mpa | |
| Tensile Stress | 断裂 | ISO 527-2 | 200 Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural Modulus | ISO 178 | 9500 Mpa | |
| Flexural Stress | ISO 178 | 280 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 1 | |
| IEC 60112 | 400 V |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 80 °C | ||
| Drying time - Hot air dryer | 2.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.20 % | ||
| Processing (Melt) Temp | 275 到 295 °C | ||
| Melt Temperature, Optimum | 285 °C | ||
| Mold Temperature | 70 到 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| Holding Pressure | 50.0 到 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 75 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.