Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 70G33HS1L-BK DUPONT USA
Zytel®
Automotive sector
Thermal stability、high strength、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : 55 到 160°C | ISO 11359-2 | 1.3E-5 cm/cm/°C |
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 261 °C |
| Linear thermal expansion coefficient | 横向 : 55 到 160°C | ISO 11359-2 | 1.4E-4 cm/cm/°C |
| Melting Temperature | ISO 11357-3 | 262 °C | |
| Linear thermal expansion coefficient | 横向 : -40 到 23°C | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 252 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 23°C | ISO 11359-2 | 2.4E-5 cm/cm/°C |
| 流动 | ISO 11359-2 | 1.8E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 8.3E-5 cm/cm/°C |
| Fill Analysis | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| Odor | VDA 270 | 3.00 | |
| Ejection Temperature | 210 °C | ||
| VDA 277 | 10.0 µgC/g |
| Injection | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| Drying time - Hot air dryer | 2.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.20 % | ||
| Processing (Melt) Temp | 275 到 295 °C | ||
| 3.00 s/mm | |||
| 100 °C | |||
| Holding Pressure | Drying Recommended | yes | |
| 12 m/min | |||
| Holding Pressure | 50.0 到 100 Mpa | ||
| Drying Temperature | 80 °C | ||
| Mold Temperature | 70 到 120 °C |
| Physical | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| Moisture Absorption | 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.8 % |
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 1.1 % |
| 流量 | ISO 294-4 | 0.30 % | |
| Moisture Absorption | 饱和, 23°C, 2.00 mm | ISO 62 | 5.7 % |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| Tensile Strain | 断裂 | ISO 527-2 | 3.0 % |
| Tensile Modulus | ISO 527-2 | 11000 Mpa | |
| Tensile Stress | 断裂 | ISO 527-2 | 200 Mpa |
| Flexural Modulus | ISO 178 | 9500 Mpa | |
| Flexural Stress | ISO 178 | 280 Mpa |
| Impact Properties | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 75 kJ/m² |
| Flammability | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| FMVSS Flammability | FMVSS 302 | B | |
| Burning Rate | 1.00 mm | ISO 3795 | 28 mm/min |
| Haze | ISO 6452 | 6.0E-4 g | |
| UL flame retardant rating | 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB |
| 0.75 mm | UL 94, IEC 60695-11-10, -20 | HB |
| Electrical Properties | Test Condition | Test Method | DUPONT USA/70G33HS1L-BK |
|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 1 | |
| IEC 60112 | 400 V |