PA6 Durethan® BKV30GH2.0 900116 LANXESS GERMANY

154

Unit Price:$2653 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
34MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical	Test Condition	Test Method	Test Result
Apparent Density		ISO60	0.60 g/cm³
Modeling Shrinkage	TD:280°C,2.00mm2	ISO294-4	0.81 %
	Modeling Shrinkage	TD:120°C,2hr,2.00mm3	ISO294-4	0.10 %
		Modeling Shrinkage	MD:280°C,2.00mm2	ISO294-4	0.29 %
		Modeling Shrinkage	Modeling Shrinkage	MD:120°C,2hr,2.00mm3	ISO294-4	0.050 %
Moisture Absorption	饱和,23°C	ISO62	7.0 %
Moisture Absorption	Moisture Absorption	平衡,23°C,50%RH	ISO62	2.1 %

Thermal Properties	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火	ISO75-2/B	219 °C
	Heat Deflection Temperature	1.8MPa,未退火	ISO75-2/A	210 °C
	Heat Deflection Temperature	Heat Deflection Temperature	8.0MPa,未退火	ISO75-2/C	150 °C
Vicat Softening Temperature		ISO306/B120	210 °C
Ball PressureTest	210°C	IEC60695-10-2	Pass
Melting Temperature		ISO11357-3	221 °C
Linear thermal expansion coefficient	MD：23到55°C	ISO11359-2	2E-05 cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	ISO11359-2	1E-04 cm/cm/°C

Additional	Test Condition	Test Method	Test Result
ISO Shortname		ISO1874	PA6,GHR,10-090,GF30

Flammability	Test Condition	Test Method	Test Result
BurningBehavior9		ISO3795	passed

Electrical Properties	Test Condition	Test Method	Test Result
Dielectric Strength	23°C,1.00mm	IEC60243-1	33 KV/mm
Comparative Tracking Index	解决方案A	IEC60112	400 V

Mechanical Properties	Test Condition	Test Method	Test Result
Tensile Modulus	23°C	ASTMD638	8730 Mpa
Tensile Modulus	Tensile Modulus	23°C	ISO527-2/1	9400 Mpa
Tensile Strength	断裂,23°C	ASTMD638	165 Mpa
Tensile Stress	断裂,23°C	ISO527-2/5	170 Mpa
Tensile Elongation	断裂,23°C	ASTMD638	3.2 %
Tensile Strain	断裂,23°C	ISO527-2/5	3.0 %
Flexural Modulus	23°C	ASTMD790	8000 Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178/A	8400 Mpa
Flexural Strength	23°C	ASTMD790	260 Mpa
Flexural Stress	3.5%Strain	ISO178/A	255 Mpa
	Flexural Stress	23°C	ISO178	260 Mpa
	Flexural Stress	Flexural Stress	FlexuralStrainatFlexuralStrength5(23°C)		3.6 %

Films Properties	Test Condition	Test Method	Test Result
Film Puncture Energy	--6	ISO6603-2	2.10 J
Film Puncture Energy	Film Puncture Energy	--7	ISO6603-2	2.20 J
Film Puncture Force	--6	ISO6603-2	744 N
Film Puncture Force	Film Puncture Force	--7	ISO6603-2	803 N

Hardness	Test Condition	Test Method	Test Result
Ball Indentation Hardness		ISO2039-1	193 Mpa

Impact Properties	Test Condition	Test Method	Test Result
Notched Izod impact strength	23°C	ISO180/1U	60 kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	55 kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	65 kJ/m²
Notched Izod impact strength	-30°C	ISO180/1U	55 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.