Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV30GH2.0 900116 LANXESS GERMANY
Durethan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| Vicat Softening Temperature | ISO306/B120 | 210 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 219 °C |
| Linear thermal expansion coefficient | TD：23to55°C | ISO11359-2 | 1E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 210 °C |
| Linear thermal expansion coefficient | MD：23到55°C | ISO11359-2 | 2E-05 cm/cm/°C |
| Heat Deflection Temperature | 8.0MPa,未退火 | ISO75-2/C | 150 °C |
| Melting Temperature | ISO11357-3 | 221 °C | |
| Ball PressureTest | 210°C | IEC60695-10-2 | Pass |
| Hardness | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 193 Mpa |
| Additional | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| ISO Shortname | ISO1874 | PA6,GHR,10-090,GF30 |
| Films Properties | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| Film Puncture Energy | --6 | ISO6603-2 | 2.10 J |
| Film Puncture Force | --6 | ISO6603-2 | 744 N |
| --7 | ISO6603-2 | 803 N | |
| Film Puncture Energy | --7 | ISO6603-2 | 2.20 J |
| Physical | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| Apparent Density | ISO60 | 0.60 g/cm³ | |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 2.1 % |
| Modeling Shrinkage | TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.10 % |
| TD:280°C,2.00mm2 | ISO294-4 | 0.81 % | |
| MD:280°C,2.00mm2 | ISO294-4 | 0.29 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 7.0 % |
| Modeling Shrinkage | MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.050 % |
| Mechanical Properties | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| Tensile Strain | 断裂,23°C | ISO527-2/5 | 3.0 % |
| Flexural Strength | 23°C | ASTMD790 | 260 Mpa |
| Tensile Modulus | 23°C | ISO527-2/1 | 9400 Mpa |
| Tensile Elongation | 断裂,23°C | ASTMD638 | 3.2 % |
| Tensile Stress | 断裂,23°C | ISO527-2/5 | 170 Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 8000 Mpa |
| Flexural Stress | 3.5%Strain | ISO178/A | 255 Mpa |
| Tensile Strength | 断裂,23°C | ASTMD638 | 165 Mpa |
| Tensile Modulus | 23°C | ASTMD638 | 8730 Mpa |
| Flexural Modulus | 23°C | ISO178/A | 8400 Mpa |
| Flexural Stress | 23°C | ISO178 | 260 Mpa |
| FlexuralStrainatFlexuralStrength5(23°C) | 3.6 % |
| Impact Properties | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 65 kJ/m² |
| Notched Izod impact strength | -30°C | ISO180/1U | 55 kJ/m² |
| 23°C | ISO180/1U | 60 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 55 kJ/m² |
| Flammability | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| ISO3795 | passed |
| Electrical Properties | Test Condition | Test Method | LANXESS GERMANY/BKV30GH2.0 900116 |
|---|---|---|---|
| Comparative Tracking Index | 解决方案A | IEC60112 | 400 V |
| Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 33 KV/mm |