ABS CYCOLAC™ FR15-NA1000 SABIC INNOVATIVE US

336

Unit Price:US$ 5,419 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance｜Flame retardant
Application Areas:small home appliances｜Automotive Applications｜Electrical applications｜composite
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	33.9 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	19 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.5 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	71.7 Mpa
Bending modulus	50.0mmSpan	ASTM D790	2720 Mpa
Tensile strain	Break	ISO 527-2/50	34 %
elongation	Break	ASTM D638	9.0 %
Tensile strain	Yield	ISO 527-2/50	2.1 %
elongation	Yield	ASTM D638	2.3 %
tensile strength	Break	ISO 527-2/50	31.3 Mpa
	tensile strength	Break	ASTM D638	35.2 Mpa
		tensile strength	Yield	ISO 527-2/50	41.3 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	41.4 Mpa
Tensile modulus		ASTM D638	2340 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8.6E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	84.1 °C
	Vicat softening temperature	--	ISO 306/B50	81.2 °C
	Vicat softening temperature	Vicat softening temperature		ASTM D15258	86.1 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	73.4 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	70.0 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	82.2 °C
RTI Elec		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI Str		UL 746	60.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
melt mass-flow rate	220°C/5.0kg	ISO 1133	10 g/10min
melt mass-flow rate	melt mass-flow rate	230°C/3.8kg	ASTM D1238	4.0 g/10min
MeltViscosity	200°C,1000sec^-1	ASTM D3835	290 Pa·s

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC7
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 4
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS CYCOLAC™ FR15-NA1000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet