PPO NORYL™ NH7010 BK1005 SABIC INNOVATIVE SHANGHAI
138
Unit Price:$4105 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Chemical resistance High rigidity
- Application Areas:Electrical applications electrical equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 300°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.25 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.050 | % | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
| Melt mass flow rate | 300°C/5.0 kg | ASTM D1238 | 10 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 38.0 | J |
| Tensile modulus | -- 2 | ASTM D638 | 2250 | Mpa |
| -- | ISO 527-2/1 | 2500 | Mpa | |
| tensile strength | Yield 3 | ASTM D638 | 68.0 | Mpa |
| Yield | ISO 527-2/50 | 69.0 | Mpa | |
| Break 3 | ASTM D638 | 49.0 | Mpa | |
| Break | ISO 527-2/50 | 63.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 5.2 | % |
| Yield | ISO 527-2/50 | 4.9 | % | |
| Break 3 | ASTM D638 | 41 | % | |
| Break | ISO 527-2/50 | 8.4 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2470 | Mpa |
| -- 5 | ISO 178 | 2520 | Mpa | |
| bending strength | -- 5, 6 | ISO 178 | 109 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 102 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ASTM D15259 | 160 | °C |
| -- | ISO 306/B50 | 161 | °C | |
| -- | ISO 306/B120 | 162 | °C | |
| RTI | UL 746 | 105 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI Elec | UL 746 | 105 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 139 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 139 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 8.2E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 8.2E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 8.2E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | ||
| Arc resistance | ASTM D495 | PLC 6 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 110 到 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 300 到 325 | °C | ||
| Mold temperature | 80 到 110 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 265 到 315 | °C | ||
| Temperature in the middle of the barrel | 275 到 320 | °C | ||
| Temperature at the front of the material cylinder | 290 到 325 | °C | ||
| Spray nozzle temperature | 300 到 325 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm, Testing by SABIC | UL 94 | V-0 | |
| 2.0 mm, Testing by SABIC | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.