Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO NH7010 BK1005 SABIC INNOVATIVE SHANGHAI
NORYL™
Electrical applications、electrical equipment
High mobility、Chemical resistance、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/NH7010 BK1005
Melt Volume-Flow Rate (MVR)
300°C/5.0 kg
ISO 1133
cm3/10min
1
Melt mass flow rate
300°C/5.0 kg
ASTM D1238
g/10 min
1
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/NH7010 BK1005
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
tensile strength
屈服 3
ASTM D638
Mpa
6
tensile strength
屈服
ISO 527-2/50
Mpa
6
tensile strength
断裂 3
ASTM D638
Mpa
4
tensile strength
断裂
ISO 527-2/50
Mpa
6
elongation
屈服 3
ASTM D638
%
5
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 3
ASTM D638
%
4
elongation
断裂
ISO 527-2/50
%
8
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
bending strength
-- 5, 6
ISO 178
Mpa
1
bending strength
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
1
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
3
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/NH7010 BK1005
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
ISO 75-2/Af
°C
1
vicat softening point
--
ASTM D15259
°C
1
vicat softening point
--
ISO 306/B50
°C
1
vicat softening point
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831, ISO 11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
8