PBT/PC VALOX™ V3900WX-BK1H078 SABIC INNOVATIVE SHANGHAI
254
Unit Price:$3667 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact Low warpage Dimensional stability High toughness Weather resistance
- Application Areas:Automotive sector Charging station Electronic and electrical Lighting applications Communication equipment Wire and cable
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.30 | g/cm³ | |
| Melt mass flow rate | 265°C/2.16kg | ASTMD1238 | 11 | g/10min |
| Melt Volume-Flow Rate (MVR) | 265°C/2.16kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.70to1.0 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.10 | % |
| density | ASTMD792 | 1.30 | g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.030 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 2200 | Mpa | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 41 | kJ/m² |
| Dart impact equipped with measuring instruments | -40°C,TotalEnergy | ASTMD3763 | 50.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 50.0 | J | |
| Bending modulus | ISO178 | 2130 | Mpa | |
| bending strength | ISO178 | 73.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 80.0 | Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 52 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 110 | J/m |
| 23°C | ASTMD256 | 800 | J/m | |
| -30°C | ISO180/1A | 8.4 | kJ/m² | |
| Tensile modulus | ISO527-2/1 | 2100 | Mpa | |
| tensile strength | 屈服 | 内部方法 | 48.0 | Mpa |
| 屈服 | ASTMD638 | 53.0 | Mpa | |
| 屈服 | ISO527-2/50 | 51.0 | Mpa | |
| 断裂 | ASTMD638 | 43.0 | Mpa | |
| 断裂 | ISO527-2/50 | 40.0 | Mpa | |
| elongation | 屈服 | ASTMD638 | 5.0 | % |
| 屈服 | ISO527-2/50 | 4.0 | % | |
| 断裂 | 内部方法 | 250 | % | |
| 断裂3 | ASTMD638 | 50 | % | |
| 断裂 | ISO527-2/50 | 42 | % | |
| Bending modulus | 50.0mm跨距 | ASTMD790 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 119 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 75.0 | °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 96.0 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 77.0 | °C | |
| vicat softening point | ASTMD152510 | 105 | °C | |
| -- | ISO306/B50 | 122 | °C | |
| -- | ISO306/B120 | 124 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8.8E-05 | cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 8.8E-05 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 9E-05 | cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| RTI Elec | UL746 | 120 | °C | |
| RTI Imp | UL746 | 120 | °C | |
| RTI Str | UL746 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 6E+16 | ohms |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| 3.0mm11 | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| 3.0mm | IEC60695-2-13 | 725 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.